Strength Testing And Material Characterization Of Cactus Spines, Mary Cooper, Jeff Goldstein, Thomas Tarlton
Strength Testing And Material Characterization Of Cactus Spines, Mary Cooper, Jeff Goldstein, Thomas Tarlton
Materials Engineering
Twelve different species of cactus spines from 6 different genera were collected from living specimens and maintained in a dry storage environment. Spines from each species underwent 3-point bend testing, XRD testing, and SEM imaging. XRD analysis was used to verify the presence of cellulose whisker like nanocrystals and to calculate the percent crystallinity of each spine. SEM images were captured of fracture surfaces at viewing angles of 90° and 45° relative to the fracture surface, with magnifications ranging between 150x and 4,000x. A total of six spines from each species were tested in three point bending using a high-resolution …
An Investigation Of Arabinan And Cellulose Based Nano-Composite Fabrication Methods, Marianne Smithfield, Carl Petterson, Robert Miller
An Investigation Of Arabinan And Cellulose Based Nano-Composite Fabrication Methods, Marianne Smithfield, Carl Petterson, Robert Miller
Materials Engineering
Microcrystalline cellulose was converted into nanocrystalline cellulose via an acid hydrolysis procedure. Scanning electron microscopy (SEM) was employed to measure the particle size and thus the effectiveness of acid hydrolysis. The nanocrystalline cellulose was poured through a 0.2μm filter to isolate the particles of ideal size. The nanocrystalline cellulose samples were stored in dimethylformamide (DMF) to prevent mold growth and agglomeration upon drying. Numerous composite samples were created by dissolving the arabinan in a solvent, suspending cellulose in the arabinan solution, and then drying the sample. Casting was performed in a silicon mold to allow sample removal without damage. Initial …