Open Access. Powered by Scholars. Published by Universities.®
Other Materials Science and Engineering Commons™
Open Access. Powered by Scholars. Published by Universities.®
- Discipline
- Institution
Articles 1 - 3 of 3
Full-Text Articles in Other Materials Science and Engineering
Comparison Of Intrusive And Non-Intrusive Methods For Corrosion Monitoring Of Fuel Processing Systems, Armando Jacob Espinoza, Thomas Conner Field
Comparison Of Intrusive And Non-Intrusive Methods For Corrosion Monitoring Of Fuel Processing Systems, Armando Jacob Espinoza, Thomas Conner Field
Materials Engineering
This presentation contains an assessment of the best overall corrosion monitoring device, intrusive or non-intrusive, for use in the petrochemical industry. Corrosion in the petrochemical industry is a large issue because it causes a deterioration of pipe integrity in fuel processing systems. A reduction of pipe wall integrity due to corrosion could result in a leak or an explosion of fuel processing lines since those systems function at high pressures. The use of corrosion monitoring systems in the petrochemical industry helps to detect early signs of corrosion prior to failure so that proper maintenance can be performed to prevent catastrophe. …
Pitting Corrosion Of 410 Stainless Steel In Hcl Solutions, Paul D. Krell
Pitting Corrosion Of 410 Stainless Steel In Hcl Solutions, Paul D. Krell
Williams Honors College, Honors Research Projects
410 stainless steel (SS) is a material used in HCl services, such as distillation column trays in oil refineries. Unlike other alloys, however, the oil refining industry lacks a good reference for the corrosion rate of 410 SS at the varying HCl concentrations and temperatures the material might experience as trays in crude unit distillation columns. The goal of this project is to fill that knowledge gap. The corrosion behavior of 410 SS in HCl environments of pH 0.50, 1.25, 2.25, 3.25, and 4.25 at temperatures of 38, 52, 79, and 93°C was investigated using several methods. Cyclic potentiodynamic polarization …
The Effects Of Carboxylic Acids In Aluminum Anodizing, Abby E. Koczera
The Effects Of Carboxylic Acids In Aluminum Anodizing, Abby E. Koczera
Honors Theses and Capstones
Hard-anodized alumina coatings were formed in sulfuric acid at low temperature and high current density in the presence of carboxylic acid additives. Citric acid, trimesic acid, mellitic acid and ethylenediaminetetraacetic acid (EDTA) were utilized in varying concentrations. The additives were chosen for their capacity to form complexes with tri-valent aluminum and hence impart chemical stability to the coatings. The coatings were sealed in boiling water, and corrosion resistance was observed in a high pH solution of potassium hydroxide. The coatings were examined using scanning electron microscopy (SEM) to assess coating thickness and pore dimensions. Thicker coatings were produced when the …