Optimization Of Porosity In Cold Spray Produced Copper And Zinc Coatings, Cameron Hughes

Graduate Theses & Non-Theses

Since its invention in 1981, the cold spray (CS) additive manufacturing (AM) process has been studied and optimized to produce well-adhered, dense material coatings. CS can operate at a wide range of temperatures if the feed material remains in a solid state. Copper and zinc were studied to characterize and understand the effects of heating element voltage, travel speed, and standoff distance on deposit porosity, grain size, microhardness, and coating thickness. Samples were sprayed on 3.2 mm x 25 mm x 150 mm 6061 aluminum substrates. Sections were taken from the middle of the samples to represent steady-state conditions. Sample …

High-Pressure Slurry Ablation For Improving Separation Of Copper/Molybdenum And Flotation Of Gold Tailings, Mitchell Harvey

Graduate Theses & Non-Theses

Disa Technologies’ High-Pressure Slurry Ablation (HPSA) is a patented particle attrition technology for the comminution and selective liberation of minerals. Two slurry streams are pumped at high pressure through opposing nozzles and collisions between solid particles suspended in the slurry streams cause breakage of the feed material. HPSA was evaluated for improving the rougher flotation of molybdenite from Cu-Mo bulk concentrate and gold-bearing pyrite from gold tailings.

Copper/molybdenum samples were provided by Montana Resources in Butte, Montana. A two-factor factorial design of experiments was used to identify HPSA operating conditions which gave the highest increase in flotation performance. Variables were …

The Tempering Response Of Cpm® 3v Tool Steel Investigated Through Tensile Testing And Microstructural Observations, Stephen A.C. Hanson

Graduate Theses & Non-Theses

Heat treatment, tensile testing failure analysis, and microstructural evaluation of the Crucible Industries tool steel CPM® 3V was undertaken to investigate CPM® 3V’s tempering response for the following samples: As-Hardened (no tempering); tempered at 450°C, 550°C, 650°C, and 700°C; and As-Received (annealed). CPM® 3V tool steel is manufactured by Crucible Industries using their proprietary Crucible Particle Metallurgy (CPM®) technology. This material was heat-treated at four different tempering temperatures and was evaluated for tensile properties according to ASTM E8. A TMS landmark tensile fixture was used to establish the ultimate tensile strength and the yield strength of the material for the …

Technical Feasibility Of Selectively Separating Rare Earth Elements By Vapor Phase Extraction And Condensation, Katie Lyons

Graduate Theses & Non-Theses

Experiments were performed to evaluate the technical feasibility of selectively separating selected rare earth halides (bromides and chlorides) using a volatilization and condensation technique. Initially, optimum chloridizing and bromidizing roast parameters were secured in studies performed on reagent grade rare earth oxide samples and subsequently confirmed in tests performed on mineral ore and concentrate samples. The volatilization and condensation experiments were performed by placing the subject rare earth halide samples in an argon-purged multiple-zone tube furnace wherein the temperature profile was controlled to establish separate vaporization and condensation regions. Following each experiment, condensate and solid residue samples were analyzed to …

Vacuum Brazing Of Diamond To Tungsten Carbide, Zhiyong Yin

Graduate Theses & Non-Theses

Diamond tools are increasingly gaining importance as cutting and drilling materials for a wide variety of industrial applications. Polycrystalline diamond (PCD) is the main ultrahard material commercially used in the oil and gas drilling industry. In this study, a reactive brazing process was developed to join polycrystalline diamond (PCD) to WC-13 wt% Co, to form the cutter for fixed-cutter drill bit applications.

Most nonmetals including polycrystalline diamond are not wet by and cannot easily be joined with conventional brazing alloys due to their chemical stability. The experimental approach was first to analyze the effect of adding an active metal (Ti, …