The Characterization And Analysis Of In-Vitro And Elevated Temperature Repassivation Of Ti-6al-4v Via Afm Techniques, Aaron J. Guerrero

Master's Theses

ABSTRACT

The Characterization and Analysis of In-vitro and Elevated Temperature Repassivation of

Ti-6Al-4V via AFM Techniques

Aaron J Guerrero

Research in the corrosion of orthopaedic implants is a growing research field where implants have been known to show adverse effects in patients who have encountered the unfortunate dissolution of their implants due to corrosion. Once corrosion begins within the body, many adverse biological reactions can occur such as late on-set infections resulting in severe health complications. The focus of this research is specifically related to the problem of late on-set infections caused by localized corrosion of orthopaedic implants. In medical …

Effectiveness Of Thermal Oxidation In Relation To Anterior Cervical Plates, Katherine A. Miyashiro

Master's Theses

Ti-6Al-4V anterior cervical plates (ACP) are used in spinal fusion surgeries to fixate cervical vertebrae during graft adhesion. However, documented cases of implant failure and the potential for ACP corrosion raise concerns regarding any degradation of material resulting from extended implantation. In addition, abrasion during implantation may damage a section of the protective oxide layer, potentially exposing surrounding tissues to the harmful effects of bare titanium, aluminum, and vanadium. Thermal oxidation has been shown to improve corrosion-resistance and wear-resistance, depending on temperature and time. To quantify the attributes of the thermally grown oxide layer, Ti-6Al-4V coupons underwent thermal oxidation treatments …