Other Materials Science and Engineering Commons^™

Computational And Experimental Study Of Structure-Property Relationships In Nial Precipitate-Strengthened Ferritic Superalloys, Shenyan Huang

Doctoral Dissertations

Ferritic superalloys strengthened by coherent ordered NiAl B2-type precipitates are promising candidates for ultra-supercritical steam-turbine applications, due to their superior resistance to creep, coarsening, oxidation, and steam corrosion as compared to Cr ferritic steels at high temperatures. Combined computational and experimental tools have been employed to investigate the interrelationships among the composition, microstructure, and mechanical behavior, and provide insight into deformation micromechanisms at elevated temperatures.

Self and impurity diffusivities in a body-centered-cubic (bcc) iron are calculated using first-principles methods. Calculated self and impurity diffusivities compare favorably with experimental measurements in both ferromagnetic and paramagnetic states of bcc Fe. The calculated …

The Effects Of Cure Schedule On Properties Of Glass-Fiber Reinforced Epoxy Matrix Composites, Trevor J. Lee

Materials Engineering

Two different two-component resin systems were cured, via Differential Scanning Calorimetry, for the times recommended by their respective manufacturers. The resin cure schedules were designed to simulate typical and attainable processing conditions; they were cured at 120°F, 140°F, and 160°F, and in-mold post-cured at 200°F, 230°F, and 260°F. The resulting scans were then compared to a baseline cure for each resin system, consisting of two heating-cooling cycles at a constant rate of temperature change. These baseline cures were then used to determine the percent cure of each sample and the shift in glass transition temperature between the baseline cure and …

Investigating The Mechanical Properties Of Compression Molded Carbon Fiber Reinforced Sheet Molding Compound, Bradley A. Jones

Materials Engineering

Callaway Golf receives a proprietary blend of prepreg material from Quantum Composites. Callaway processes the prepreg in-house and supplied 254mm x 254mm x 1.3mm panels of carbon fiber sheet molding compound (CFSMC) for characterizing. Tensile strength was analyzed by conducting tensile tests per ASTM D3039. Tensile coupons were cut to 254mm long by 25.4mm wide. Tabs were constructed from 1.6mm thick GFRP printed circuit board material. A commercial grade two part epoxy was used to bond the tabs to the CFSMC. Tensile results were inconclusive due to consistent fractures occurring outside the gauge lengths of the specimens.

Flexure strength was …