Full-Text Articles in Other Materials Science and Engineering
Artificial Muscle Project: Process Development Of Polydimethyl Siloxane Thin Films For Use In Dielectric Electroactive Polymer Artificial Muscle Actuators, Vincent J. Gayotin, Richard W. Morrison, Paul A. Preisser
Artificial Muscle Project: Process Development Of Polydimethyl Siloxane Thin Films For Use In Dielectric Electroactive Polymer Artificial Muscle Actuators, Vincent J. Gayotin, Richard W. Morrison, Paul A. Preisser
Materials Engineering
An artificial muscle design was created founded on the principles of a dielectric electroactive polymer (DEAP), which is fundamentally similar to a capacitor. A polydimethyl siloxane (PDMS)-based elastomer, Sylgard 184 from Dow Corning, was chosen for the design and spun coat onto polystyrene (PS) Petri dishes at varying speeds to create a thin film, using speeds of 2000 rpm, 3000 rpm, 4000 rpm, 5000 rpm, and 6000 rpm. The film thicknesses were measured optically through use of a microscope with coupled computer imaging software to generate a characteristic curve of film thickness to spin speed, achieving a minimum film thickness …
The Effects Of Cure Schedule On Properties Of Glass-Fiber Reinforced Epoxy Matrix Composites, Trevor J. Lee
The Effects Of Cure Schedule On Properties Of Glass-Fiber Reinforced Epoxy Matrix Composites, Trevor J. Lee
Materials Engineering
Two different two-component resin systems were cured, via Differential Scanning Calorimetry, for the times recommended by their respective manufacturers. The resin cure schedules were designed to simulate typical and attainable processing conditions; they were cured at 120°F, 140°F, and 160°F, and in-mold post-cured at 200°F, 230°F, and 260°F. The resulting scans were then compared to a baseline cure for each resin system, consisting of two heating-cooling cycles at a constant rate of temperature change. These baseline cures were then used to determine the percent cure of each sample and the shift in glass transition temperature between the baseline cure and …