Interfaces In Dynamic Brittle Fracture Of Pmma: A Peridynamic Analysis, Longzhen Wang, Javad Mehrmashhadi, Florin Bobaru
Interfaces In Dynamic Brittle Fracture Of Pmma: A Peridynamic Analysis, Longzhen Wang, Javad Mehrmashhadi, Florin Bobaru
Department of Mechanical and Materials Engineering: Faculty Publications
Recent experiments in bonded PMMA layers have shown dramatic changes in dynamic crack growth characteristics depending on the interface location and toughness. In this paper we present a peridynamic (PD) analysis of this phenomenon and determine three elements that are essential in a model reproducing the observed fracture behavior: (1) softening near the crack tip to account for changes in PMMA due to heat-generation induced by the high strain rates reached around the crack tip in dynamic fracture; (2) independent extension (mode I) and shear (mode II) modes of fracture; (3) a two-parameter fracture model, which matches both strength and …
Peridynamic Model For Dynamic Fracture In Unidirectional Fiber-Reinforced Composites, Wenke Hu, Youn Doh Ha, Florin Bobaru
Peridynamic Model For Dynamic Fracture In Unidirectional Fiber-Reinforced Composites, Wenke Hu, Youn Doh Ha, Florin Bobaru
Florin Bobaru Ph.D.
We propose a computational method for a homogenized peridynamics description of fiber-reinforced composites and we use it to simulate dynamic brittle fracture and damage in these materials. With this model we analyze the dynamic effects induced by different types of dynamic loading on the fracture and damage behavior of unidirectional fiber-reinforced composites. In contrast to the results expected from quasi-static loading, the simulations show that dynamic conditions can lead to co-existence of and transitions between fracture modes; matrix shattering can happen before a splitting crack propagates. We observe matrix–fiber splitting fracture, matrix cracking, and crack migration in the matrix, including …
Peridynamic Model For Dynamic Fracture In Unidirectional Fiber-Reinforced Composites, Wenke Hu, Youn Doh Ha, Florin Bobaru
Peridynamic Model For Dynamic Fracture In Unidirectional Fiber-Reinforced Composites, Wenke Hu, Youn Doh Ha, Florin Bobaru
Department of Mechanical and Materials Engineering: Faculty Publications
We propose a computational method for a homogenized peridynamics description of fiber-reinforced composites and we use it to simulate dynamic brittle fracture and damage in these materials. With this model we analyze the dynamic effects induced by different types of dynamic loading on the fracture and damage behavior of unidirectional fiber-reinforced composites. In contrast to the results expected from quasi-static loading, the simulations show that dynamic conditions can lead to co-existence of and transitions between fracture modes; matrix shattering can happen before a splitting crack propagates. We observe matrix–fiber splitting fracture, matrix cracking, and crack migration in the matrix, including …