Biaxial Bending And Lateral-Torsional Instability Of Imperfect Frp I-Beams Including Effects Of Retrofitting, Jodi Marie Knorowski
Biaxial Bending And Lateral-Torsional Instability Of Imperfect Frp I-Beams Including Effects Of Retrofitting, Jodi Marie Knorowski
Civil & Environmental Engineering Theses & Dissertations
This thesis presents the outcome of a theoretical and experimental study of the behavior of Fiber Reinforced Polymer (FRP) I-beams susceptible to lateral-torsional instability or when subjected to biaxial bending. Laboratory experiments involved application of vertical and horizontal static loads to a 4 x 4 x ¼ in. I-beam with various lengths, and the resulting displacement, twist, and strain were recorded. In the vertical direction, the beam was loaded from different reference load heights with respect to the shear center of the beam. The governing biaxial flexure and torsion differential equations were modified to account for the presence of initial …
Optical Detection Of Melting Point Depression For Silver Nanoparticles Via In Situ Real Time Spectroscopic Ellipsometry, S. A. Little, T. Begou, R. W. Collins, S. Marsillac
Optical Detection Of Melting Point Depression For Silver Nanoparticles Via In Situ Real Time Spectroscopic Ellipsometry, S. A. Little, T. Begou, R. W. Collins, S. Marsillac
Electrical & Computer Engineering Faculty Publications
Silver nanoparticle films were deposited by sputtering at room temperature and were annealed while monitoring by real time spectroscopic ellipsometry (SE). The nanoparticle dielectric functions (0.75 eV-6.5 eV) obtained by SE were modeled using Lorentz and generalized oscillators for the nanoparticle plasmon polariton (NPP) and interband transitions, respectively. The nanoparticle melting point could be identified from variations in the oscillator parameters during annealing, and this identification was further confirmed after cooling through significant, irreversible changes in these parameters relative to the as-deposited film. The variation in melting point with physical thickness, and thus average nanoparticle diameter, as measured by SE …