Articles 1 - 2 of 2
Full-Text Articles in Other Electrical and Computer Engineering
High Electron Mobility In Algan/Gan Heterostructures Grown On Bulk Gan Substrates, E. Frayssinet, W. Knap, P. Lorenzini, N. Grandjean, J. Massies, C. Skierbiszewski, T. Suski, I. Grzegory, S. Porowski, Grigory Simin, X. Hu, M. Asif Khan, M. S. Shur, R. Gaska, D. Maude
High Electron Mobility In Algan/Gan Heterostructures Grown On Bulk Gan Substrates, E. Frayssinet, W. Knap, P. Lorenzini, N. Grandjean, J. Massies, C. Skierbiszewski, T. Suski, I. Grzegory, S. Porowski, Grigory Simin, X. Hu, M. Asif Khan, M. S. Shur, R. Gaska, D. Maude
Faculty Publications
Dislocation-free high-quality AlGaN/GaN heterostructures have been grown by molecular-beam epitaxy on semi-insulating bulk GaN substrates. Hall measurements performed in the 300 K–50 mK range show a low-temperature electron mobility exceeding 60 000 cm2/V s for an electron sheet density of 2.4×1012 cm−2. Magnetotransport experiments performed up to 15 T exhibit well-defined quantum Hall-effect features. The structures corresponding to the cyclotron and spin splitting were clearly resolved. From an analysis of the Shubnikov de Hass oscillations and the low-temperature mobility we found the quantum and transport scattering times to be 0.4 and 8.2 ps, respectively. The …
Optical Bandgap Formation In Alingan Alloys, G. Tamulaitis, K. Kazlauskas, S. Juršėnas, A. Žukauskas, M. A. Khan, J. W. Yang, J. Zhang, Grigory Simin, M. S. Shur, R. Gaska
Optical Bandgap Formation In Alingan Alloys, G. Tamulaitis, K. Kazlauskas, S. Juršėnas, A. Žukauskas, M. A. Khan, J. W. Yang, J. Zhang, Grigory Simin, M. S. Shur, R. Gaska
Faculty Publications
We report on the spectral dynamics of the reflectivity, site-selectively excited photoluminescence,photoluminescence excitation, and time-resolved luminescence in quaternary AlInGaN epitaxial layers grown on GaN templates. The incorporation of a few percents of In into AlGaN causes significant smoothening of the band-bottom potential profile in AlInGaN layers owing to improved crystal quality. An abrupt optical bandgap indicates that a nearly lattice-matched AlInGaN/GaN heterostructure with large energy band offsets can be grown for high-efficiency light-emitting devices.