Refining Particle Size Specification For Asphalt Emulsion, Pedro Luis Diaz Romero

Graduate Theses and Dissertations

Pavements begin to deteriorate as soon as they are constructed, and traffic is released. The rate at which a pavement deteriorates depends on the material quality, the environment, and the loads carried. To properly preserve pavements and extend their life, various pavement preservation treatments are used. For flexible pavements, a considerable number of these treatments use asphalt emulsion (which are refer to simply emulsions from here on). Emulsions are classified based on their particle charge and reactivity. Emulsions used in chip seals are usually of rapid set reactivity and are classified based on tests over fifty years old.

It has …

Comparing The Stiffness Of Cold In-Place Recycled Asphalt Pavement To Hot Mix Asphalt: Determining The Reproducibility Of The Stiffness Rebound Test, Tanner Turben

Civil Engineering Undergraduate Honors Theses

The Stiffness Raveling Mechanism Test (SRMT) was originally developed as an indirect measure of pavement stiffness to determine a pavement’s tendency to ravel, a type of damage. Regarding rehabilitation of existing roadways by Full Depth Reclamation (FDR) Cold In-Place Recycling (CIR), concern of field repeatability was expressed (Hill & Braham, 2016).

An analysis of lab-compacted samples of CIR and Hot Mix Asphalt (HMA) was performed to determine if the results could be reproduced between CIR and HMA. Additionally, the experiment observed the effects of percent air voids, temperature, and moisture conditioning on CIR and HMA. Three samples were prepared for …

Evaluation Of Fracture Principles In Asphalt Concrete Utilizing The Sc(B) Geometry, Airam Marlee Morales Vega

Graduate Theses and Dissertations

Since cracking is one of the principal distresses to be considered in asphalt concrete, multiple fracture tests and geometries have been used to quantify cracking resistance. One of the most popular geometries that have been used in fracture tests is the Semi-Circular bend (SC(B)). However, for this geometry, most of the fracture test methods use different parameters such as thickness, testing temperatures, and loading rates. Thus, the purpose of this research was first to evaluate fracture energy by performing a ruggedness test based on ASTM E1169. Then, to apply fracture mechanics concepts to evaluate three specimen thicknesses (25, 50, and …