Effect Of Fly Ash Fortification In The Manufacture Process Of Making Concrete Towards Characteristics Of Concrete In Sulfuric Acid Solution, Asep Handaya Saputra, Muhammad Shohibi, Masatoshi Kubouchi
Effect Of Fly Ash Fortification In The Manufacture Process Of Making Concrete Towards Characteristics Of Concrete In Sulfuric Acid Solution, Asep Handaya Saputra, Muhammad Shohibi, Masatoshi Kubouchi
Makara Journal of Technology
Fly ash is a silica or alumino silica material that can be used as a constituent of cement in the concrete manufacturing process. Utilization of fly ash aims to improve durability and minimize the reduction of concrete’s compressive strength exposed to an acidic environment, which can be achieved through the pozzolanic reaction of fly ash with Ca(OH)2 within concrete. The reduced content of Ca(OH)2 through pozzolanic reaction will minimize the tendency of ettringite formation (compounds that cause deterioration and decrease the compressive strength of concrete). In order to determine the relation between fly ash replenishment into concrete with concrete’s characteristics …
Surface Treatment Of Fly Ash For Improving The Tensile Strength Of Fly Ash/Unsaturated Polyester Composites, Sugiman Sugiman, Paryanto Dwi Setyawan
Surface Treatment Of Fly Ash For Improving The Tensile Strength Of Fly Ash/Unsaturated Polyester Composites, Sugiman Sugiman, Paryanto Dwi Setyawan
Makara Journal of Technology
The paper presents the surface treatment of fly ashes using acid and alkali solution on the tensile strength of the fly ash/unsaturated polyester (UP) composites. Sulfuric acid (H2SO4), hydrofluoric acid (HF) and sodium hydroxide (NaOH) solution with concentration of 0%, 5%, 10%, 15%, and 20% (by weight) were used for surface treatment of fly ashes. Generally, the tensile strength of the treated fly-ash/UP composites shows a significant increase compared to the untreated fly ash. Of all surface treatments studied, the optimum tensile strength was obtained at a concentration of 10%. At this concentration, at a fly ash content of 30% …