Interfacial Stability Of Electrodeposition Of Cuprous Oxide Thin Films, Partho Neogi
Interfacial Stability Of Electrodeposition Of Cuprous Oxide Thin Films, Partho Neogi
Chemical and Biochemical Engineering Faculty Research & Creative Works
Experiments on deposition of Cu2O films from basic cupper sulfate solution show that copper also deposits. At low, but basic values of pH only copper deposits and at high pH only cuprous oxide deposits. In the intermediate range where both compete the system shows oscillations at "constant current." Linear stability analysis has been conducted for such an electrochemical cell to show that oscillations can take place in the parameter space identified in the experiments. The results are keeping with most of the experimental observations, which are many, but not with all. The physical mechanisms behind the oscillations are …
Development Of Novel Method For Preparation Of Pemfc Electrodes, Hansung Kim, Branko N. Popov
Development Of Novel Method For Preparation Of Pemfc Electrodes, Hansung Kim, Branko N. Popov
Faculty Publications
A method based on pulse electrodeposition technique was developed for preparation of membrane electrode assemblies (MEAs). In this approach, platinum is deposited directly on the surface of the carbon electrode. The method ensures most of the platinum to be in close contact with the membrane. Using this method it is possible to increase the Pt/C ratio up to 75 wt % near the surface of the electrode resulting in a 5 µm thick catalyst layer. The MEA prepared by pulse electrodeposition exhibits a current density of 0.33 A/cm2 at 0.8 V with platinum loading of 0.25 mg of Pt/cm …
Electrodeposition Of Feconicu Quaternary System, Qiang Huang
Electrodeposition Of Feconicu Quaternary System, Qiang Huang
LSU Doctoral Dissertations
Electrodeposition is a cost-effective method to produce thin film materials, which have been used widely in the microelectronic industry, and is advantageous to fabricate metal deposits into recessed and curved areas. In this dissertation, FeCoNiCu quaternary alloy system was investigated, both experimentally and theoretically, for fabrication of multilayers, grating structures, and nanowires. Multilayer structures are composed of alternating ferromagnetic and nonmagnetic nanometric layers, and are of interest due to the giant magnetoresistance (GMR) property it possesses, a change in electric resistance in the presence of an external magnetic field. In addition, the compositional modulation, or the composition contrast, in multilayer …