Biomaterials Commons^™

Tin-Silver As A Novel Biodegradable Metallic Biomaterial, Charley Goodwin

All Dissertations

The Essure device is a non-hormonal, minimally-invasive, permanent female sterilization implant, removed from the market due to an increase in adverse events, hypothesized to be caused by corrosion of the Sn-Ag component of the implant. The goals of this dissertation were to first develop implant retrieval methods for Essure devices and surrounding tissue, documenting signs of degradation and metallic degradation products, then to characterize the electrochemical behavior of Sn-Ag in biologically representative environments and finally, to assess the biological interaction of Sn-Ag. Retrieval analyses developed successful methods, qualifying the degree of corrosion, primarily of the Sn-Ag component and finding Sn …

Corrosion Of Stainless Steel 316l And Astm F75 Cobalt Chromium Alloy During Immersion Testing In Silver Salt Solutions, Meagan Higgins

Materials Engineering

This study evaluates the potential effects of silver salts on biocompatible metals used for prostheses during the chemical reduction process to produce a silver antimicrobial layer on the metal’s surface. Samples of two biocompatible metals were obtained: Stainless Steel 316L and ASTM F75 Cobalt Chromium Alloy. Three different silver salts were also acquired: silver nitrate, silver sulfadiazine, and silver chloride. Specimens of each metal were cut to size using a 4-1/2 inch aluminum oxide, 40 grit, cut off wheel for metal, attached to a Dewalt Angle Grinder. The biocompatible metal samples were then subject to either Solution 1, water with …

The Effect Of Particle Surface Area To Volume Ratio On Ion Release From Cocr Spheres, Darin J. Grandfield

Master's Theses

In 2005, over 200,000 Americans underwent a hip arthroplasty, the replacement of a hip joint with an artificial prosthesis. Of these arthroplasties, metal-on-metal type implants represent an increasing usage percentage. Metal-on-metal implants are selected largely for their low volumetric wear rate, durability, and resistance to corrosion. In spite of these advantages, little is known concerning the long-term consequences of heavy metal alloy use in the body, although early research indicates potentially carcinogenic results. This thesis is a preliminary investigation into these long term effects and their root causes.

An improved comprehension of the corrosion kinetics and the rate of ion …