Mode I Fracture Toughness Of Eight-Harness-Satin Carbon Cloth Weaves For Co-Cured And Post-Bonded Laminates, Josh E. Smith
Mode I Fracture Toughness Of Eight-Harness-Satin Carbon Cloth Weaves For Co-Cured And Post-Bonded Laminates, Josh E. Smith
Master's Theses
Mode I interlaminar fracture of 3k 8-Harness-Satin Carbon cloth, with identical fill and weft yarns, pre-impregnated with Newport 307 resin was investigated through the DCB test (ASTM D5528). Crack propagations along both the fill and weft yarns were considered for both post-bonded (co-bonded) and co-cured laminates. A patent-pending delamination insertion method was compared to the standard Teflon film option to assess its applicability to mode I fracture testing. The Modified Beam Theory, Compliance Calibration method, and Modified Compliance Calibration method were used for comparative purposes for these investigations and to evaluate the validity of the proposed Equivalent Stiffness (EQS) method. …
Investigation Of Astm E 238 Bearing Pin Properties For Various Aerospace Alloys, Trevor J. Lee
Investigation Of Astm E 238 Bearing Pin Properties For Various Aerospace Alloys, Trevor J. Lee
Master's Theses
Aircraft are often designed with numbers determined by testing in a lab, rather than by repeatedly building prototypes. These lab tests conform to testing specifications so that the numbers can be compared between manufacturers, suppliers, and lab technicians. One such specification is ASTM specification E238 – 84(08), and it is used to determine important properties of a bearing pin joint like hinges, bolt holes, and rivet joints. The properties determined from this fastener-through-plate method are bearing strength, bearing yield strength, and bearing stiffness.
Adhering to the methods outlined in ASTM E238, a study was performed, looking at the effects that …