Full-Text Articles in Physics
Magnetic And Transport Properties Of Nimnal Thin Films, Andriy Vovk, Minghui Yu, Leszek Malkinski, Charles O'Connor, Zhenjun Wang, Eden Durant, Jinke Tang, Vladimir Golub
Magnetic And Transport Properties Of Nimnal Thin Films, Andriy Vovk, Minghui Yu, Leszek Malkinski, Charles O'Connor, Zhenjun Wang, Eden Durant, Jinke Tang, Vladimir Golub
Jinke Tang
The magnetic and transport properties of Ni2MnAl thin films prepared using pulse laser deposition were investigated. It was shown that the films are granular and multiphase. Contrary to the data reported earlier we observe nonmonotonic temperature dependence of resistance with minimum in the vicinity of 100 K for the films deposited on substrates held at 773 K and negative magnetoresistance (MR) values of about 2.5% at 5 K and 1.6% at RT in magnetic field of 50 kOe. These values of MR are the highest reported up to date for Ni2MnAl films. Large negative MR in …
Ultrafine Nife2o4 Powder Fabricated From Reverse Microemulsion Process, Jiye Fang, Narayan Shama, Le Duc Tung, Eun Young Shin, Charles J. O'Connor, Kevin L. Stokes, Gabriel Caruntu, John B. Wiley, Leonard Spinu, Jinke Tang
Ultrafine Nife2o4 Powder Fabricated From Reverse Microemulsion Process, Jiye Fang, Narayan Shama, Le Duc Tung, Eun Young Shin, Charles J. O'Connor, Kevin L. Stokes, Gabriel Caruntu, John B. Wiley, Leonard Spinu, Jinke Tang
Jinke Tang
NiFe2O4 ultrafine powder with high crystallinity has been prepared through a reverse microemulsion route. The composition in starting solution was optimized, and the resulting NiFe2O4 was formed at temperature of around 550–600 °C, which is much lower than that observed from the solid-state reaction. Magnetic investigation indicates that samples are soft-magnetic materials with low coercivity and with the saturation magnetization close to the bulk value of Ni ferrite.