Analysis And Differentiation Of Uniform And Localized Corrosion Of Cu, Roshan J. Daljeet
Analysis And Differentiation Of Uniform And Localized Corrosion Of Cu, Roshan J. Daljeet
Electronic Thesis and Dissertation Repository
The current plan for disposal of used nuclear fuel in Canada involves sealing the waste in steel containers coated with 3 mm of copper and burying them in a deep geologic repository (DGR). The purpose of the copper coating is to provide corrosion resistance. To achieve long term containment, it is necessary that the copper layer corrodes slowly and predictably via active dissolution rather than passivating due to film formation. Film formation could allow pitting corrosion to occur in early phase repository conditions when groundwater ions such as Cl– , SO4 2– and HCO3 – play a dominant role in …
Investigating The Corrosion Behaviour Of Ni-Based Alloys In Industrially Relevant Environments, Jeffrey D. Henderson
Investigating The Corrosion Behaviour Of Ni-Based Alloys In Industrially Relevant Environments, Jeffrey D. Henderson
Electronic Thesis and Dissertation Repository
Typical engineering materials may experience high corrosion rates when exposed to aggressive service conditions. Such conditions include high concentrations of aggressive anions and oxidants, high solution acidity, and/or high temperatures. Alloys with high corrosion resistance may be selected to avoid material failure caused by corrosion, for example, Ni-Cr-Mo alloys. These alloys exhibit excellent corrosion resistance due to the formation of a passive oxide film, primarily containing Cr and Mo. However, film breakdown can result in localized corrosion, e.g., crevice corrosion. Localized corrosion processes can penetrate deep into the bulk alloy, threatening its integrity. While the oxide film and localized …