Effects Of Bonding Pressure And Lamina Thickness On Mechanical Properties Of Clt Composed Of Southern Yellow Pine, Cody S. Bates
Effects Of Bonding Pressure And Lamina Thickness On Mechanical Properties Of Clt Composed Of Southern Yellow Pine, Cody S. Bates
Theses and Dissertations
This study produced cross-laminated timber panels at a range of four lamina thickness (5/8, 1, 1 1/8, and 1 1/4 inch) and three bonding pressures (50, 125, 200 psi), producing a total of 12 panels for mechanical testing. The goal of this study is to observe how the thickness and pressure trends affect the mechanical properties of CLT. Tests include flatwise bending, flatwise shear, internal-bond, and delamination. Results showed that bending MOE decreases as the panel thickness increases while bonding pressure had no significance. Bending MOR was less significant for the thickness and more significant for pressure compared to the …
Study Of Alloy And Process Modifications To Design Hydrogen Resilient High Hardness Steels, William R. Williams
Study Of Alloy And Process Modifications To Design Hydrogen Resilient High Hardness Steels, William R. Williams
Theses and Dissertations
High hardness steels (HHS) are vulnerable to hydrogen embrittlement, which can lead to rapid degradation of mechanical properties. Improved resistance to hydrogen embrittlement would be beneficial to many industries including construction, automotive, and military. A comparison study was performed to assess the hydrogen susceptibility of select commercially available and in-house designed HHS alloys. Slow strain rate tensile tests, performed with specimens charged with various levels of hydrogen, provided a macroscopic view of the onset of hydrogen embrittlement. Hydrogen permeation and thermal desorption spectroscopy tests determined the uptake and diffusivity of hydrogen through the material. The evaluation of hydrogen susceptibility for …