Stress Corrosion Cracking Resistance Of Cold-Sprayed Al 6061 Deposits Using A Newly Developed Test Fixture, Mala M. Sharma, Jeremy Schreiber, Timothy Eden, Victor Champagne
Stress Corrosion Cracking Resistance Of Cold-Sprayed Al 6061 Deposits Using A Newly Developed Test Fixture, Mala M. Sharma, Jeremy Schreiber, Timothy Eden, Victor Champagne
Faculty Journal Articles
The stress corrosion cracking (SCC) response of Al 6061 bulk deposits produced by high-pressure cold spray (HPCS) was investigated and compared to commercial wrought Al 6061-T6 material. Representative tensile coupons were stressed to 25%, 65% and 85% of their respective yield strength and exposed to ASTM B117 salt fog for 90 days. After exposure, the samples were mechanically tested to failure, and subsequently investigated for stress corrosion cracking via optical and scanning electron microscopy with energy-dispersive X-ray spectroscopy (EDS). The results were compared to the wrought Al 6061-T6 properties and correlated with the observed microstructures. Wrought samples showed the initiation …