Pulsed Laser Beam Welding Of Pd43Cu27Ni10P20 Bulk Metallic Glass, Ling Shao, Amit Datye, Jiankang Huang, Jittisa Ketkaew, Sung Woo Sohn, Shaofan Zhao, Sujun Wu, Yuming Zhang, Udo D. Schwarz, Jan Schroers
Pulsed Laser Beam Welding Of Pd43Cu27Ni10P20 Bulk Metallic Glass, Ling Shao, Amit Datye, Jiankang Huang, Jittisa Ketkaew, Sung Woo Sohn, Shaofan Zhao, Sujun Wu, Yuming Zhang, Udo D. Schwarz, Jan Schroers
Electrical and Computer Engineering Faculty Publications
We used pulsed laser beam welding method to join Pd43Cu27Ni10P20 (at.%) bulk metallic glass and characterized the properties of the joint. Fusion zone and heat-affected zone in the weld joint can be maintained completely amorphous as confirmed by X-ray diffraction and differential scanning calorimetry. No visible defects were observed in the weld joint. Nanoindentation and bend tests were carried out to determine the mechanical properties of the weld joint. Fusion zone and heat-affected zone exhibit very similar elastic moduli and hardness when compared to the base material, and the weld joint shows high …
Mechanical Characterization Of Parts Produced By Ceramic On‐Demand Extrusion Process, Amir Ghazanfari, Wenbin Li, Ming Leu, Gregory Hilmas
Mechanical Characterization Of Parts Produced By Ceramic On‐Demand Extrusion Process, Amir Ghazanfari, Wenbin Li, Ming Leu, Gregory Hilmas
Faculty Publications, Mechanical Engineering
Ceramic On‐Demand Extrusion (CODE) is an additive manufacturing process recently developed to produce dense three‐dimensional ceramic components. In this paper, the properties of parts produced using this freeform extrusion fabrication process are described. High solids loading (~60 vol%) alumina paste was prepared to fabricate parts and standard test methods were employed to examine their properties including the density, strength, Young's modulus, Weibull modulus, toughness, and hardness. Microstructural evaluation was also performed to measure the grain size and critical flaw size. The results indicate that the properties of parts surpass most other ceramic additive manufacturing processes and match conventional fabrication techniques.