Full-Text Articles in Applied Mechanics
Jcati Base Plate, Jacob Atamian
Jcati Base Plate, Jacob Atamian
All Undergraduate Projects
Students of the Mechanical Engineering Technology (MET) program at Central Washington University have contributed to an ongoing Carbon Fiber Recycler project funded by the Joint Center for Aerospace Technology Innovation (JCATI). The goal of this project was to modify the existing recycling system to produce a higher success rate of recycled carbon composite material. This report focuses on increasing the rigidity of the crushing gears so that the deflection occurring among the components during operation was below 0.005 inches to ensure proper operating conditions. The operating speed of the crushing gears was 2.5 rpm with a crushing load of 10,500 …
The Limits & Effects Of Draw On Properties And Morphology Of Pan-Based Precursor And The Resultant Carbon Fibers, Sarah Edrington
The Limits & Effects Of Draw On Properties And Morphology Of Pan-Based Precursor And The Resultant Carbon Fibers, Sarah Edrington
Theses and Dissertations--Mechanical Engineering
The process, structure, and property relationship of PAN fiber as a precursor to carbon fiber was studied. The limitations of stable spinning and property improvement associated with hot draw in solution spinning were found and quantified. Conditions were varied to generated precursor fiber up to the limit of draw, from which actual samples were collected for thermal conversion to carbon fiber. Samples of PAN and subsequent carbon fiber were characterized using tensile testing and x-ray analysis. The effects of draw on modulus and break stress, as well as the orientation of the crystalline structure of both parent precursor and resultant …
Finite Element Modeling Of Delamination Damage In Carbon Fiber Laminates Subject To Low-Velocity Impact And Comparison With Experimental Impact Tests Using Nondestructive Vibrothermography Evaluation, George Rodriguez Iv
Master's Theses
Carbon fiber reinforced composites are utilized in many design applications where high strength, low weight, and/or high stiffness are required. While composite materials can provide high strength and stiffness-to-weight ratios, they are also more complicated to analyze due to their inhomogeneous nature. One important failure mode of composite structures is delamination. This failure mode is common when composite laminates are subject to impact loading.
Various finite element methods for analyzing delamination exist. In this research, a modeling strategy based on contact tiebreak definitions in LS-DYNA®was used. A finite element model of a low-velocity impact event was created to …
Biaxial & Twist Testing Of Composite Carbon-Fiber Sandwich Panels For Automotive Racing Vehicles, Erik Eckberg
Biaxial & Twist Testing Of Composite Carbon-Fiber Sandwich Panels For Automotive Racing Vehicles, Erik Eckberg
Materials Engineering
Composite sandwich panels were constructed with 4-ply plain weave carbon-fiber/epoxy face sheets in the 0o/45o/0o/45o orientation and 1/8th inch Nomex honeycomb core. The panels were cut into 5-inch square test plates for mechanical testing. All testing was done on a fixture designed and fabricated by Pratt & Miller Engineering and installed on an Instron testing system at Cal Poly. The twist test was performed by supporting diagonal corners of the plate while simultaneously loading the opposite two corners at a crosshead rate of .06 in/min (ASTM 3044-94R11). Out of 10 panels tested, …