Preliminary Investigation Into The Cause Of Pinhole Porosity In Aluminum Metal Castings From Serpentine Impurities In Olivine Sand, Brodie J. Biersner
Preliminary Investigation Into The Cause Of Pinhole Porosity In Aluminum Metal Castings From Serpentine Impurities In Olivine Sand, Brodie J. Biersner
Dissertations and Theses @ UNI
The problem addressed in this study is how contaminates in the foundry molding aggregate olivine, affect aluminum castings during the casting process. This research will concentrate on hydrated contaminates, specifically the mineral serpentine. The purpose of this research is to better understand how hydrated minerals contribute to the generation of pinhole porosity defects during the casting process. Understanding how impurities in foundry aggregates affect the casting process would aid in the reduction of scrap caused by core and molding sands, ultimately providing savings to the casting manufacturer.
A foundry grade olivine was compared to a new source of olivine to …
The Effects Of Post Inoculant Additions On Ductile Iron Fade, Travis James Frush
The Effects Of Post Inoculant Additions On Ductile Iron Fade, Travis James Frush
Dissertations and Theses @ UNI
This study involved the investigation of three specific, commercially available, post inoculants for ductile iron and their effect on the magnesium fading rate and chill reducing tendency in a low volume production environment. Although fading effects of ductile iron have been extensively investigated, in general, they apply to high volume production operations. Unfortunately, for the smaller foundry operations, many of the process solutions proposed for the prevention of the fading effects are not applicable or practical. In addition to the small production operations, new process technologies are also excluded from many of these process solutions. For this reason, a study …
Development Of An Automated Ultrasonic Inspection Cell For Detecting Subsurface Discontinuities In Cast Iron, John Scott Burningham
Development Of An Automated Ultrasonic Inspection Cell For Detecting Subsurface Discontinuities In Cast Iron, John Scott Burningham
Dissertations and Theses @ UNI
Manufacturing of value added products by companies in todays global marketplace requires the vendors to meet certain minimum standards, SAE, ASTM, ISO, etc. In a global economy, as a manufacturer for the year 2000 and beyond, preferred vendors will become ISO 9000 certified to maintain a market share of produced goods.
An automated inspection cell was developed for the inspection of cast iron ports to detect subsurface discontinuities. The cell consists of an ultrasonic flaw detector (UFD), transducer, robot, immersion tank, computer, and software. Normal beam pulse-echo ultrasonic nondestructive testing is performed on each rough casting.
Using test blocks and …