Full-Text Articles in Metallurgy
Corrosion Inhibitors: Mitigating The Degradation Of Rebar, Jake R. Hughes
Corrosion Inhibitors: Mitigating The Degradation Of Rebar, Jake R. Hughes
Williams Honors College, Honors Research Projects
Our conjecture was twofold: first, that two compounds historically used as food preservatives could act as environmentally friendly inhibitors against rebar corrosion, and second, that molecular properties have a quantifiable influence on inhibition efficiency (%IE). To evaluate the two compounds, cyclic potentiodynamic polarization was used to determine corrosion current density (icorr) and %IE. The “green” inhibitor candidates included sodium metabisulfite and ascorbic acid, which yielded maximum %IE values of -123900% and 91%, respectively. Results indicated that sodium metabisulfite is not a suitable inhibitor, while ascorbic acid showed potential to extend reinforced concrete’s design life without posing health or …
Interfacial Corrosion Of Copper And The Formation Of Copper Hydroxychloride, Mary Teague, Shengxi Li, Hongbo Cong
Interfacial Corrosion Of Copper And The Formation Of Copper Hydroxychloride, Mary Teague, Shengxi Li, Hongbo Cong
Williams Honors College, Honors Research Projects
Electrical circuitry is an industry, among many others, heavily using the element of copper. Ensuring the mechanical integrity of Cu is crucial, especially in salt environments, for the multifaceted composition of circuits. 4N NaCl solution (equilibrium concentration in ~84% RH) simulated this three-phase system. Rectangular Cu samples were partially immersed in both ambient and continuous lab air sparging atmospheres to understand waterline corrosion of the metal. Open circuit potentials (OCP) were continuously taken during the immersion testing for a maximum of 5 days. A scanning electron microscopy (SEM) equipped with an energy dispersive X-ray spectrometer (EDS), Raman spectroscopy, and 3-D …