Effects Of Graphene On Electrochemical Behaviors Of Ni(Oh)2 As Supercapacitor Material, Zhen-Zhen Zhao, Wen-Bin Ni, Neng-Yue Gao, Hong-Bo Wang, Jian-Wei Zhao
Effects Of Graphene On Electrochemical Behaviors Of Ni(Oh)2 As Supercapacitor Material, Zhen-Zhen Zhao, Wen-Bin Ni, Neng-Yue Gao, Hong-Bo Wang, Jian-Wei Zhao
Journal of Electrochemistry
The enhanced electrochemical properties of Ni(OH)2 by the oxidation defected graphene were studied by both experimental method and theoretical calculation. The composite material of nano-Ni(OH)2/graphene was prepared by potentiostatic deposition on the graphene substrate. Observed by TEM, the Ni(OH)2 nanoparticles were well dispersed on the graphene substrate with the diameter of 5.0±0.5 nm. The capacitance of the system measured by the electrochemical test was 1928 F?g-1. As indicated by the theoretical calculations, the composite material becomes conductive since Ni(OH)2 is combined with surface functional groups of the graphene through the strong chemical interaction. The electrons transfer from the graphene substrate …
Electrochemical Double-Layer Capacitors Using Phenolic Resin-Based Carbon Fibers, Rong Xue, Jing-Wang Yan, Ying Tian, Bao-Lian Yi
Electrochemical Double-Layer Capacitors Using Phenolic Resin-Based Carbon Fibers, Rong Xue, Jing-Wang Yan, Ying Tian, Bao-Lian Yi
Journal of Electrochemistry
Phenolic resin-based activated carbon fiber(ACF) was prepared by KOH activation.The electrochemical properties of pulverized phenolic resin-based carbon fiber(P-ACF) were examined in 6 mol·L-1 KOH compared with that of the original ACF.P-ACF exhibited a better capacitive behavior and showed a larger specific capacitance(200 F·g-1) as well as a lower capacitance decrease at high current densities.The pore resistance for ion migration(Rp) in P-ACF was lower(2.96 Ω) than that in ACF(4.65 Ω).Pulverization increased the exposure of the cross section,lowered the contact resistance between the carbon fibers and decreased the pore resistance for ion migration.
Synthesis Of Mesoporous Nickel Oxide For Supercapacitor Application, Xuan-Xuan Chen, Zhen-Zhen Zhao, Deng-Chao Wang, Zhong-Jie Huang, Wen-Bin Ni, Li Yu, Jian-Wei Zhao
Synthesis Of Mesoporous Nickel Oxide For Supercapacitor Application, Xuan-Xuan Chen, Zhen-Zhen Zhao, Deng-Chao Wang, Zhong-Jie Huang, Wen-Bin Ni, Li Yu, Jian-Wei Zhao
Journal of Electrochemistry
Mesoporous nickel oxide has been synthesized by calcining metal-organic coordination precursor.Transmission electron microscopy and BET test showed that the prepared NiO had a regular morphology and displayed a narrow size distribution.Electrochemical tests revealed that such mesoporous NiO had a specific capacity of 72 F·g-1 at the current of 2.0 A·g-1.Futhermore,the material showed excellent cycle-life stability.There was no degradation of capacitance after 1000 cycles.