Preparation And Characterization Of The Lani0.6fe0.4o3-Δ Cathode For Intermediate Temperature Solid Oxide Fuel Cell, Hang Liu, Bo Huang, Xin-Jian Zhu

Journal of Electrochemistry

The LaNi0.6Fe0.4O3-δ as cathode material for intermediate temperature solid oxide fuel cell was prepared using a combustion synthesis technique. The X-ray diffraction (XRD) pattern showed that the single-phase LaNi0.6Fe0.4O3-δ perovskite could be obtained after heat treatment at 600°C. The TEM and SEM images of the synthesized powders revealed that the grains were 50-100nm. According to the electrochemical impedance spectra (EIS), the polarization resistance of the symmetric cell LaNi0.6Fe0.4O3-δ/ScSZ/LaNi0.6Fe0.4O3-δ sintered at 1050°C was the smallest (0.70Ω?cm2, 0.27Ω?cm2 and 0.12Ω?cm2 at 750°C, 800°C and 850°C, respectively). In the presence of the Fe-Cr alloy interconnection at 750°C, the cathode performance showed that, with …

Evaluation Of Cathode Materials For Low Temperature (500-700c) Solid Oxide Fuel Cells, Alexander M. Lassman

Master's Theses

Solid oxide fuel cells (SOFC) have gained a great deal of interest, due to their potential for high efficiency power generation and ability to utilize hydrogen fuel, as well as various hydrocarbon-based fuels. A recent trend in SOFC development has been towards lower operating temperatures (500-700°C), which can substantially reduce the cost and complexity of the system. This thesis presents an investigation into state of the art Ba- and La- based cathode materials for use in low temperature (500-700°C) solid oxide fuel cells.

Synthesis of A-site deficient [A=0.97] Ba_0.5Sr_0.5Co_0.8Fe_0.2O₃ (BSCF) was …