Articles 1 - 2 of 2
Full-Text Articles in Electrical and Computer Engineering
The Sol-Gel Synthesis And Electrochemical Performance Of Li_3v_2(Po_4)_3/C Cathode Material For Lithium Ion Battery, Li-Ying Liu, Lian Chen, Hai-Yan Zhang, Yu-Chun Zhai
The Sol-Gel Synthesis And Electrochemical Performance Of Li_3v_2(Po_4)_3/C Cathode Material For Lithium Ion Battery, Li-Ying Liu, Lian Chen, Hai-Yan Zhang, Yu-Chun Zhai
Journal of Electrochemistry
Li3V2(PO4)3/C was synthesized by sol-gel method with citric acid as chelate and C sources.Physical and electrochemical performances of as-prepared materials were characterized through XRD,SEM and galvanostatic charge-discharge tests,etc.The results showed that products produced by calcining at 800 ℃ for 12 h had a single phase crystal structure and relatively small particle sizes with uniform distribution.At 0.1 C,0.5 C and 1 C,the initial specific discharge capacities were 153.0,143.1 and 130.6 mAh·g-1,respectively,and capacity efficiencies were 93.1%,85.4% and 77.3% after 50 cycles,respectively.Charge efficiencies were all above 80% and discharge voltages were higher.
Dye Sensitized Solar Cell With Conventionally Annealed And Post-Hydrothermally Treated Nanocrystalline Semiconductor Oxide Tio2 Derived From Sol-Gel Process, Akhmad Herman Yuwono, Badrul Munir, Alfian Ferdiansyah, Arif Rahman, Wulandari Handini
Dye Sensitized Solar Cell With Conventionally Annealed And Post-Hydrothermally Treated Nanocrystalline Semiconductor Oxide Tio2 Derived From Sol-Gel Process, Akhmad Herman Yuwono, Badrul Munir, Alfian Ferdiansyah, Arif Rahman, Wulandari Handini
Makara Journal of Technology
Dye-sensitized solar cell (DSSC) is one of the very promising alternative renewable energy sources to anticipate the declination in the fossil fuel reserves in the next few decades and to make use of the abundance of intensive sunlight energy in tropical countries like Indonesia. In the present study, TiO2 nanoparticles of different nanocrystallinity was synthesized via sol−gel process with various water to inorganic precursor ratio (Rw) of 0.85, 2.00 and 3.50 upon sol preparation, followed with subsequent drying, conventional annealing and post-hydrothermal treatments. The resulting nanoparticles were integrated into the DSSC prototype and sensitized with an organic dye made of …