Relating Surface Resistivity To Corrosion Of Rebar Embedded In Portland Cement Concrete, Luisa Alejandra Morales

Open Access Theses & Dissertations

Reinforced concrete is widely used as a construction material known for its durability and proficiency of withstanding large forces in severe environments. Despite that the majority of these structures result in long-term performance, there is still a large number of failures of reinforced concrete structures as a result in corrosion of the reinforcement and concrete degradation. It is critical to assess the state of the corroded structure to decide on whether maintaining or replacing the structure is needed. The objective of this study is to characterize a relationship between the steel reinforcement corrosion and the concrete's resistivity. It is widely …

Evaluation Of Orthophosphate Based Corrosion Inhibitors In Treated Water For El Paso Region, Francisco Solis Jr

Open Access Theses & Dissertations

Corrosion is an electrochemical phenomenon that involves the deterioration of a metal by the reaction of itself with its surrounding environment. One of the greatest issues for water utilities around the country is to keep the water quality safe. Corrosion can affect the quality of the water that we use on a daily basis by adding a bad taste, increasing the concentration of heavy metals, and allowing outside contaminants to enter the distribution system. The use of phosphate based corrosion inhibitors was tested in two different metals: iron and copper. The phosphate in the inhibitors react with the calcium in …

Assessing Corrosivity Of Galvanized Soil Reinforcements From Electrochemical Tests, Diana Alejandra Cabrera

Open Access Theses & Dissertations

The accurate estimation of the service lives of mechanically stabilized earth (MSE) walls requires a proper evaluation of the corrosion potential through electrochemical test methods. Robust field tests are required to assess the corrosivity of galvanized metal used in MSE walls. To simulate an environment similar to an MSE wall, cylindrical soil specimens about 12 in. (300 mm) in diameter and 10 in. (250 mm) in height were constructed. For every specimen, two instruments were used. The first instrument measured the polarization resistance corrosion tests carried out on galvanized strips and meshes, as well as epoxy-coated rebars. The second instrument …

Microstructural Investigation Of Vintage Pipeline Steels Highly Susceptible To Stress Corrosion Cracking, Monica Adriana Torres

Open Access Theses & Dissertations

The use of pipelines for the transmission of gas offers not only efficiency, but a number of economic advantages. Nevertheless, pipelines are subject to aggressive operating conditions and environments which can lead to in-service degradation [1] and thus to failures. These failures can have catastrophic consequences, such as environmental damage and loss of life [2]. One of the most dangerous threats to pipeline integrity is stress corrosion cracking (SCC). Despite the substantial progress that has been achieved in the field, due to the complex nature of this phenomenon there is still not a complete understanding of this form of external …

The Effects Of Uncommon Silicides On The Oxidation Of Alloys From The Nb-Cr-Si System, Daniel Brendan Voglewede

Open Access Theses & Dissertations

Niobium based alloys are being tapped as potential successors to current nickel base superalloys in high temperature applications. In the aerospace industry, high temperature materials are constantly being pushed to higher temperature regimes in order to improve engine efficiency however current superalloys cannot be pushed further due to melting temperature limitations. Niobium, being a refractory metal, can withstand much higher temperatures than nickel however its oxidation properties are woefully inadequate.

The purpose of this study is to ascertain whether increased silicon additions can improve niobium oxidation properties by: forming ternary silicides with better oxidation properties and by preventing the formation …