Effect Of Thermal Exposure On Tensile Strength And Microhardness Of Welded And Precipitation Hardened Rx82 Aluminum Alloy Extrusions In The T4 And T6 Conditions, Lucien Miller
Materials Engineering
This investigation is focused on the effect paint-bake cycles have on the tensile strength and microhardness of GMAW welded RX82 aluminum extrusions in T4 and T6 base conditions. To simulate the paint-bake cycle, T4 and T6 RX82 aluminum samples were GMAW welded and heat treated at 350°F, 390°F, and 425°F for durations of 30 minutes, 1.0 hour, and 2.0 hours, with five replicates for each treatment. Microhardness profiles of T4 samples treated at 350°F for 30 minutes and 1.0 hour display weld/HAZ HV values of 86.04 and 82.51 respectively, followed by maximums of 123.21 and 121.10. Average ultimate tensile strength …
High Cycle Rotating Bending Fatigue Of 6061-T6 Friction Stir Welded Extrusions, John Chang, Travis Miller
High Cycle Rotating Bending Fatigue Of 6061-T6 Friction Stir Welded Extrusions, John Chang, Travis Miller
Materials Engineering
Fatigue testing was done on friction stir welded joints of 6061-T6 aluminum extrusions. Tests were run using a rotating bending fatigue machine at stresses from 111.5 to 138.7 MPa. Failures occurred on the order of 105 to 107 cycles, and an S-N curve was generated based off of the failure results. After the samples failed, the location of the failure and the number of cycles to failure were noted. Fatigue samples were designed in SolidWorks with a tapered 2 inch reduced section. The 2 inch reduced section will include the entire weld region as seen from the microhardness …