A Rubric For Electrochemical Testing Of Metallic Biomaterials, Frederick G. De La Fuente
A Rubric For Electrochemical Testing Of Metallic Biomaterials, Frederick G. De La Fuente
Master's Theses
Corrosion is a major factor for the failure of metallic medical implants. Testing a metal’s suseptability to corrosion prior to implantation is key to a successful implantation. Electrochemical processes were used in this study to evaluate the characteristics of corrosion of both AISI 316 stainless steel and titanium alloy Ti6Al4V, welded and non-welded. Linear, potentiodynamic, and cyclic polarization curves were produced by the PARC 2273 potentiostat showing the corrosion tendencies of the metals in four unique solutions 3.5% NaCl, 0.35% NaCl, phosphate buffered saline solution (PBS), and Butterfield phosphate buffered solution (BPS). The concentration of chloride ions in solutions affected …
Tribological Comparison Of Traditional And Advanced Firearm Coatings, Greg Boban
Tribological Comparison Of Traditional And Advanced Firearm Coatings, Greg Boban
Master's Theses
The objective of this project is to find which type of coating has the best performance characteristics for finishing firearms. This is accomplished by measuring and comparing several performance characteristics, such as: adhesion, hardness, wear resistance, friction control, and corrosion resistance. Appearance is not a factor since any exterior coating that is flashy can be subdued or camouflaged with special purpose paints, which have proven durable enough for such purposes. Cost will not be a limiting factor for this experiment, but will be discussed in the conclusion as a secondary concern. This data will be used to identify the best …
The Effect Of Particle Surface Area To Volume Ratio On Ion Release From Cocr Spheres, Darin J. Grandfield
The Effect Of Particle Surface Area To Volume Ratio On Ion Release From Cocr Spheres, Darin J. Grandfield
Master's Theses
In 2005, over 200,000 Americans underwent a hip arthroplasty, the replacement of a hip joint with an artificial prosthesis. Of these arthroplasties, metal-on-metal type implants represent an increasing usage percentage. Metal-on-metal implants are selected largely for their low volumetric wear rate, durability, and resistance to corrosion. In spite of these advantages, little is known concerning the long-term consequences of heavy metal alloy use in the body, although early research indicates potentially carcinogenic results. This thesis is a preliminary investigation into these long term effects and their root causes.
An improved comprehension of the corrosion kinetics and the rate of ion …
Effectiveness Of Thermal Oxidation In Relation To Anterior Cervical Plates, Katherine A. Miyashiro
Effectiveness Of Thermal Oxidation In Relation To Anterior Cervical Plates, Katherine A. Miyashiro
Master's Theses
Ti-6Al-4V anterior cervical plates (ACP) are used in spinal fusion surgeries to fixate cervical vertebrae during graft adhesion. However, documented cases of implant failure and the potential for ACP corrosion raise concerns regarding any degradation of material resulting from extended implantation. In addition, abrasion during implantation may damage a section of the protective oxide layer, potentially exposing surrounding tissues to the harmful effects of bare titanium, aluminum, and vanadium. Thermal oxidation has been shown to improve corrosion-resistance and wear-resistance, depending on temperature and time. To quantify the attributes of the thermally grown oxide layer, Ti-6Al-4V coupons underwent thermal oxidation treatments …