A New Method Of Producing High Strength Oil Palm Shell Lightweight Concrete, Hilmi Mahmud
A New Method Of Producing High Strength Oil Palm Shell Lightweight Concrete, Hilmi Mahmud
Hilmi Mahmud
This paper presents a new method to produce high strength lightweight aggregate concrete (HSLWAC) using an agricultural solid waste, namely oil palm shell (OPS). This method is based on crushing large old OPS. Crushed OPS are hard and have a strong physical bond with hydrated cement paste. The 28 and 56. days compressive strength achieved in this study were about 53 and 56. MPa, respectively. Furthermore, it was observed that it was possible to produce grade 30 OPS concrete without the addition of any cementitious materials. Compared to previous studies, significantly lower cement content was used to produce this grade …
Shear Behaviour Of Reinforced Palm Kernel Shell Concrete Beams, Hilmi Mahmud
Shear Behaviour Of Reinforced Palm Kernel Shell Concrete Beams, Hilmi Mahmud
Hilmi Mahmud
The shear behaviour of palm kernel shell concrete (PKSC) beams prepared using palm kernel shell (PKS) as lightweight aggregate (LWA) is reported here. The shear strength of grade 30 PKSC with a density of 1850 kg/m(3) was found 24% higher than the corresponding normal weight concrete (NWC). Good aggregate interlock in PKSC was evident as it produced shorter jagged cracks compared to longer plain cracks of NWC. Further, PKSC was able to produce twice as many flexural and shear cracks compared to NWC. Tension stiffening between the tensile cracks of PKSC enhanced flexural rigidity and dowel action. The non-linear numerical …
Enhancement And Prediction Of Modulus Of Elasticity Of Palm Kernel Shell Concrete, Hilmi Mahmud
Enhancement And Prediction Of Modulus Of Elasticity Of Palm Kernel Shell Concrete, Hilmi Mahmud
Hilmi Mahmud
This paper presents results of an investigation conducted to enhance and predict the modulus of elasticity (MOE) of palm kernel shell concrete (PKSC). Scanning electron microscopic (SEM) analysis on palm kernel shell (PKS) was conducted. Further, the effect of varying sand and PKS contents and mineral admixtures (silica fume and fly ash) on compressive strength and MOE was investigated. The variables include water-to-binder (w/. b) and sand-to-cement (s/. c) ratios. Nine concrete mixes were prepared, and tests on static and dynamic moduli of elasticity and compressive strength were conducted. The SEM result showed presence of large number of micro-pores on …
High-Strength Rice Husk Ash Concrete Incorporating Quarry Dust As A Partial Substitute For Sand, Hilmi Mahmud
High-Strength Rice Husk Ash Concrete Incorporating Quarry Dust As A Partial Substitute For Sand, Hilmi Mahmud
Hilmi Mahmud
Quarry dust is a by-product from the granite crushing process in quarrying activities. This paper presents the findings from experimental work undertaken to evaluate the suitability of quarry dust as a partial substitute for sand in high-strength concrete (HSC) containing rice husk ash (RHA). Two grades of HSC mixes, to achieve 60 MPa and 70 MPa at 28 days, were designed with and without the incorporation of RHA. Quarry dust was then used in the mixes containing RHA as a partial substitute for sand, in quantities ranging from 10% to 40%. The slump of the fresh concrete and the compressive …
Understanding The Effects Of Addition Of Copper Nanoparticles To Sn-3.5 Ag Solder
Understanding The Effects Of Addition Of Copper Nanoparticles To Sn-3.5 Ag Solder
A.S. Md Abdul Haseeb
Purpose - The purpose of this paper is to focus on the fabrication of SAC nanocomposites solder and discuss the effects of nanoCu addition on the structure and properties of resulted nanocomposite solder. Design/methodology/ approach - Ball milling is a nonequilibrium processing technique for producing composite metal particles with submicron homogeneity by the repeated cold welding and fracture of powder particles. This method is believed to offer good processablity, precise control over the solder composition, and produce more homogeneous mixture. Findings - It is found that the melting temperature, the wetting behaviour, and hardness are improved when the Cu nanoparticles …