Vacuum Infusion Of Composites: Durability Of Hybrid Large Area Additive Tooling For Vacuum Infusion Of Composites, Nathan Northrup, Jason Weaver, Andy R. George
Vacuum Infusion Of Composites: Durability Of Hybrid Large Area Additive Tooling For Vacuum Infusion Of Composites, Nathan Northrup, Jason Weaver, Andy R. George
Faculty Publications
The durability of a hybrid large area additively manufactured fiberglass ABS mold for vacuum infusion of composites was evaluated. The validation was done by designing and fabricating a mold for a custom test artifact and analyzing the surface geometry over the course of multiple infusions until tool failure. After printing and machining, the mold required a sealer to maintain vacuum integrity. The mold was able to produce 10 parts successfully before the sealed tool surface began to tangibly roughen, resulting in increased difficulty of demolding and a rougher surface finish. After the 14th infusion, the part required destructive force to …
Effect Of Heat Treatment On Microstructure And Hardness Of A Worn Rail Repaired Using Laser Powder Deposition, Ershad Mortazavian, Zhiyong Wang, Hualiang Teng
Effect Of Heat Treatment On Microstructure And Hardness Of A Worn Rail Repaired Using Laser Powder Deposition, Ershad Mortazavian, Zhiyong Wang, Hualiang Teng
Mechanical Engineering Faculty Research
The frequent replacement of worn rails on tracks brings an immense economic burden on the railroad industry, and also causes significant interruptions to railroad operation. Restoration of worn rails via laser powder deposition (LPD) can considerably reduce the associated maintenance costs. This study was focused on the use of LPD to repair the worn profile of a standard U.S. rail. The microstructure of the 304L stainless steel deposits with a minimum hardness of 85 HRB was composed of austenite, δ-ferrite, and sigma. Micropores were dispersed throughout the deposit, and microcracks were found at the rail-deposition interface. The pearlitic rail substrate …