Heating Power Of Coated Fecov Magnetic Nanoparticles, Hanaa Ali Alshammari

Browse all Theses and Dissertations

The effect of coatings on the heating curves of magnetic nanoparticles was studied in this Thesis. Iron cobalt vanadium (FeCoV) nanoparticles with oxide (CoOFe2O3) and graphite (C) coating to prevent oxidation, were synthesized through thermal plasma processing method. The magnetic nanoparticles had an average diameter of 30 nm. In the case of FeCoV with oxide coating, the initial diameter of the pure FeCoV nanoparticles on average was 30 nm but after oxidation 5 nm thick oxide layer was created. As a result of this oxidation, the magnetic core of FeCoV nanoparticles was shrunk from 30 nm to 20 nm in …