Identification And Characterization Of The Iron-Zinc Intermetallics Formed In Galvanneal Steel, Richard Frederick George Grant
Identification And Characterization Of The Iron-Zinc Intermetallics Formed In Galvanneal Steel, Richard Frederick George Grant
Physics Theses & Dissertations
The demand to improve the corrosion resistance of steel sheet, particularly for use within the automotive industry, has led to a dramatic increase in the use of coated steels in place of cold-rolled sheet steel. Galvanneal steel results from the post annealing of the zinc-coated steel sheet, in which iron and zinc are interdiffused to form an iron-zinc alloy coating. Within this alloy coating, four main iron-zinc phases, Zeta, Delta, Gamma-1, and Gamma may be present. Manufacture of the most suitable coating requires identifying which phases form during the galvannealing process, an understanding of the properties of each phase and …
Investigation Of The Platinum-Rich Portion Of The Platinum-Tantalum Phase Diagram, Bob Dean Browning
Investigation Of The Platinum-Rich Portion Of The Platinum-Tantalum Phase Diagram, Bob Dean Browning
Theses and Dissertations
The Pt-Ta binary system was investigated at two isotherms;1000°C and 1500°C, and at eleven alloy compositions in the range of 50 to 100 atomic percent platinum. The alloys were examined by x-ray diffraction and metallography. Three intermetallic compounds, Pt2Ta, Pt3Ta, and Pt4Ta were found to exist in this composition range. The Pt4Ta intermetallic appeared only at the 1500°C isotherm. Platinum dissolved tantalum substitutionally to 90 atomic percent at 1500 °C and to approximately 80 atomic percent at 1000 °C.