Structure And Magnetic Properties Of The Mnbi Low Temperature Phase, Jinbo Yang, William B. Yelon, William Joseph James, Qingsheng Cai, Samit Roy, Naushad Ali
Structure And Magnetic Properties Of The Mnbi Low Temperature Phase, Jinbo Yang, William B. Yelon, William Joseph James, Qingsheng Cai, Samit Roy, Naushad Ali
Physics Faculty Research & Creative Works
High purity MnBi low temperature phase has been prepared and analyzed using magnetic measurements and neutron diffraction. The low-temperature phase of the MnBi alloy has a coercivity μ0iHc of 2.0 T at 400 K, and exhibits a positive temperature coefficient from 0 to at least 400 K. The neutron data refinement indicated that the Mn atom changes its spin direction from c axis above room temperature to nearly perpendicular to the c axis at 50 K. A canted magnetic structure has been observed below 200 K. The anisotropy field increases with increasing temperature which gives rise to …
Magnetic And Mössbauer Studies On Oxygen Deficient Perovskite, La₀.₆Sr₀.₄Feo3-Δ, Jinbo Yang, William B. Yelon, William Joseph James, X.-D. Zhou, Yixiang Xie, Harlan U. Anderson, Zili Chu
Magnetic And Mössbauer Studies On Oxygen Deficient Perovskite, La₀.₆Sr₀.₄Feo3-Δ, Jinbo Yang, William B. Yelon, William Joseph James, X.-D. Zhou, Yixiang Xie, Harlan U. Anderson, Zili Chu
Physics Faculty Research & Creative Works
Samples of La0.6Sr0.4Fe3-δ with varying oxygen vacancy contents were prepared by heating them in different gas flows. Magnetization measurement showed that samples with low oxygen vacancies have a magnetic ordering temperature in the range of 300-325 K while those with 9%-12% oxygen vacancies have a magnetic ordering temperature of 800 K and higher. Mössbauer spectra at 300 K exhibit paramagnetic or weak magnetic characteristics for the N2, O2, and air-quenched samples, whereas an average hyperfine field of 52 T is found for the CO/CO2 reduced samples. The heat treatment in …
Effect Of Oxygen Vacancies On The Magnetic Structure Of The La₀.₆Sr₀.₄Feo3-Δ Perovskite: A Neutron Diffraction Study, Zili Chu, William B. Yelon, Jinbo Yang, William Joseph James, Harlan U. Anderson, Yixiang Xie, Satish K. Malik
Effect Of Oxygen Vacancies On The Magnetic Structure Of The La₀.₆Sr₀.₄Feo3-Δ Perovskite: A Neutron Diffraction Study, Zili Chu, William B. Yelon, Jinbo Yang, William Joseph James, Harlan U. Anderson, Yixiang Xie, Satish K. Malik
Physics Faculty Research & Creative Works
Magnetic interactions in perovskite compounds of the type La1-xSrxMO3-δ (M=3d transition such as Mn and Fe) are presumed to arise through a super exchange between 3d electrons of the magnetic ions via oxygen orbitals. The magnetic structure of La0.6Sr0.4FeO3-δ has been studied with neutron diffraction. Oxygen vacancies were created by annealing samples under various gases including N2, air and mixtures of CO/CO2. All La0.6Sr0.4FeO3-δ compounds maintain the rhombohedral structure (space group R3̄c). The air- or oxygen-annealed samples have almost no oxygen …