Diffuse Absorbing Beryllium Coatings Produced By Magnetron Sputtering, David D. Allred, C. M. Egert

Faculty Publications

Beryllium coatings with varying thicknesses and columnar grain sizes were deposited by low temperature magnetron sputtering and wet chemically etched to enhance diffuse absorption of light. After etching these coatings exhibited a matte black surface finish and low specular reflectance (below 2%) in the IR up to a critical wavelength dependent upon the original grain size of the coating. Extremely thick coatings (350 µm) with original grain sizes of 10 to 12 µm were produced which exhibited specular reflectances below 0.5% up to 50 µm wavelength and a Lambertian BRDF at 10.6 µm averaging 4.3x10-3 ster-1. Scanning electron micrographs are …