Size Dependence Of Static And Dynamic Magnetic Properties In Nanoscale Square Permalloy Antidot Arrays, Minghui Yu, Leszek Malkinski, Leonard Spinu, Weillie Zhou, Scott Whittenburg
Size Dependence Of Static And Dynamic Magnetic Properties In Nanoscale Square Permalloy Antidot Arrays, Minghui Yu, Leszek Malkinski, Leonard Spinu, Weillie Zhou, Scott Whittenburg
Physics Faculty Publications
Permalloy antidot arrays with different square hole sizes (1200×1200, 800×800, and 400×400 nm2) have been fabricated by means of electron-beam lithography and lift-off techniques. The smaller square hole size results in enhanced remanence and reduced coercivity in the antidot array. Multiple resonance modes were clearly observed for the magnetic field applied normal to the array plane, and double uniform resonance modes occurred when the field deviated more than 30° from the normal to the plane. Two distinct dipolar field patterns with different orientations and magnitudes split the uniform resonance into double resonance modes. The double resonance modes show …
Microwave Absorption Of Patterned Arrays Of Nanosized Magnetic Stripes With Different Aspect Ratios, Leszek M. Malkinski, Minghui Yu, Andriy Y. Voyk, Donald J. Scherer Ii, Leonard Spinu, Weillie Zhou, Scott Whittenburg, Zachary Davis, Jin-Seung Jung
Microwave Absorption Of Patterned Arrays Of Nanosized Magnetic Stripes With Different Aspect Ratios, Leszek M. Malkinski, Minghui Yu, Andriy Y. Voyk, Donald J. Scherer Ii, Leonard Spinu, Weillie Zhou, Scott Whittenburg, Zachary Davis, Jin-Seung Jung
Physics Faculty Publications
Arrays consisting of nanosized stripes of Permalloy with different length-to-width ratios have been fabricated using electron beam nanolithography, magnetron sputtering, and lift-off process. These stripes have a thickness of 100 nm, a width of 300 nm, and different lengths ranging from 300 nm to 100 μm. The stripes are separated by a distance of 1 μm. Magnetization hysteresis loops were measured using a superconducting quantum interference device susceptometer. Microwave absorption at 9.8 GHz was determined by means of ferromagnetic resonance technique. The dependence of the resonant field on the angle between the nanostructure and the in-plane dc magnetic …