Structure And Magnetism Of Multiphase Sm0.080co0.645fe0.276 Powders, V. G. Harris, M. Liou, B. N. Das, V. M. Browning, J. E. Snyder, M. Rubinstein, S. H. Lawrence, R. Littleton Iii, D. P. Pappas
Structure And Magnetism Of Multiphase Sm0.080co0.645fe0.276 Powders, V. G. Harris, M. Liou, B. N. Das, V. M. Browning, J. E. Snyder, M. Rubinstein, S. H. Lawrence, R. Littleton Iii, D. P. Pappas
Physics Publications
A Sm-poor mixture of Fe-substituted Sm2Co17, having the nominal stoichiometry of Sm0.080Co0.645Fe0.276, was ball-milled to explore the possibility of enhancing its remanence through direct microstructural refinement. With milling, the Sm2(Co0.7Fe0.3)17 compound disassociates to a body-centered-cubic supersaturated SmCoFe solid solution and a residual SmCoFe amorphous phase. Correspondingly, the coercive field values first increase, peaking at 0.83 kOe after 180 min of milling, then decrease with continued milling to