The Incorporation Of Graphene To Lithium Cobalt Oxide As A Cathode To Improve The Performance Of Lithium Ion Batteries, Kenan Wang

Graduate Theses and Dissertations

One of the objectives of this thesis work was to investigate the cathode performance of lithium cobalt oxide (LiCoO2) incorporated with graphene powder in lithium ion batteries (LIBs). Graphene powder was incorporated into cathode materials to enhance the performance of LIBs. The other objective was to impede the construction of a solid electrolyte interphase (SEI) sheet using graphene sheet coating on its cathode.

The results of this work show that adding graphene powder improved the performance of LiCoO¬2 as a cathode material. With the incorporation of different weight percentages of graphene powder, the LiBs showed distinct changes in their charging …

Nanostructural Origin Of Semiconductivity And Large Magnetoresistance In Epitaxial Nico2O4/Al2O3 Thin Films, Congmian Zhen, Xiaozhe Zhang, Wengang Wei, Wenzhe Guo, Ankit Pant, Xiaoshan Xu, Jian Shen, Li Ma, Denglu Hou

Xiaoshan Xu Papers

Despite low resistivity (~1 mΩ cm), metallic electrical transport has not been commonly observed in inverse spinel NiCo₂O₄, except in certain epitaxial thin films. Previous studies have stressed the effect of valence mixing and the degree of spinel inversion on the electrical conduction of NiCo₂O₄ films. In this work, we studied the effect of nanostructural disorder by comparing the NiCo₂O₄ epitaxial films grown on MgAl₂O₄ (1 1 1) and on Al₂O₃ (0 0 1) substrates. Although the optimal growth conditions are similar for the …

Induced Ferromagnetism In Multilayered Graphene In Proximity With Cofe2o4, Himanshu Verma, Dereje Seifu, Shashi P. Karna, Haiping Hong, Mohindar S. Seehra

Faculty & Staff Scholarship

Composites of anisotropic diamagnetic multilayer Graphene (MLG) and ferrimagnetic CoFe2O4 (CFO) nanoparticles (NPs) were synthesized through a one-step sonication process in the presence of a surfactant. The samples were characterized at ambi- ent using x-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM), Raman spectroscopy, magnetic force microscopy (MFM) and magnetometry (vibrating sample magnetometer). An induced ferromagnetism was observed in MLG with saturation magnetization MS = 18 emu/g(MLG). This induced ferromagnetism is attributed to ferrimagnetic CFO uniformly distributed on the surface of diamagnetic MLG. SEM images confirm uniform dense distribu- tion of CFO nanoparticles on MLG. MFM images …