Metamaterials and photonic crystals are engineered composites that exhibit electromagnetic properties superior to those found in nature. They have been shown to produce novel and useful phenomena that allow extraordinary control over the electromagnetic field. One of these phenomena is self-collimation, an effect observed in photonic crystals in which a beam of light propagates without diffraction and is forced to flow in the direction of the crystal. Self-collimation however, like many of the mechanisms enabled through dispersion engineering, is effective in directions only along the principal axes of the lattice. To this effect, a general purpose synThesis procedure was developed …
Degenerate Parallel Conducting Layer And Conductivity Type Conversion Observed From P-Ge1 - YSnY (Y = 0.06%) Grown On N-Si Substrate, Mee-Yi Ryu, Yung Kee Yeo, M. Ahoujja, Thomas R. Harris, Richard T. Beeler, John Kouvetakis
Degenerate Parallel Conducting Layer And Conductivity Type Conversion Observed From P-Ge1 - YSnY (Y = 0.06%) Grown On N-Si Substrate, Mee-Yi Ryu, Yung Kee Yeo, M. Ahoujja, Thomas R. Harris, Richard T. Beeler, John Kouvetakis
Faculty Publications
Electrical properties of p-Ge1−ySny (y = 0.06%) grown on n-Si substrate were investigated through temperature-dependent Hall-effect measurements. It was found that there exists a degenerate parallel conducting layer in Ge1−ySny/Si and a second, deeper acceptor in addition to a shallow acceptor. This parallel conducting layer dominates the electrical properties of the Ge1−ySny layer below 50 K and also significantly affects those properties at higher temperatures. Additionally, a conductivity type conversion from p to n was observed around 370 K for this sample. A two-layer conducting model was used …
Effect Of Ga Content On Defect States In Cuin1-XGaXSe2 Photovoltaic Devices, Jennifer T. Heath, J. David Cohen, William N. Shafarman, Dongxiang Liao, Angus Rockett
Effect Of Ga Content On Defect States In Cuin1-XGaXSe2 Photovoltaic Devices, Jennifer T. Heath, J. David Cohen, William N. Shafarman, Dongxiang Liao, Angus Rockett
Faculty Publications
Defects in the band gap of CuIn1-xGaxSe2 have been characterized using transient photocapacitance spectroscopy. The measured spectra clearly show response from a band of defects centered around 0.8 eV from the valence band edge as well as an exponential distribution of band tail states. Despite Ga contents ranging from Ga/(In+Ga)=0.0 to 0.8, the defect bandwidth and its position relative to the valence band remain constant. This defect band may act as an important recombination center, contributing to the decrease in device efficiency with increasing Ga content.