Surface Morphology Of Laser-Superheated Pb(111) And Pb(100), Z. H. Zhang, Bo Lin, X. L. Zeng, H. E. Elsayed-Ali
Surface Morphology Of Laser-Superheated Pb(111) And Pb(100), Z. H. Zhang, Bo Lin, X. L. Zeng, H. E. Elsayed-Ali
Electrical & Computer Engineering Faculty Publications
The surface step density on the vicinal Pb(111) and the surface vacancy density on Pb(100) after laser superheating and melting are investigated using reflection high-energy electron diffraction. With ∼100-ps laser pulses, Pb(111) surface superheating does not significantly change the density of the steps and step-edge roughness. However, after laser surface melting, the average terrace width and the string length at the step edge become as large as those at room temperature. The average terrace width at 573 K changes from 38±15 to 64±19 Å after laser surface melting, while the average string length at the step edge changes from 90±14 …
Temperature Dependence Of Step Density On Vicinal Pb(111), Z. H. Zhang, H. E. Elsayed-Ali
Temperature Dependence Of Step Density On Vicinal Pb(111), Z. H. Zhang, H. E. Elsayed-Ali
Electrical & Computer Engineering Faculty Publications
The temperature dependence of step density on the vicinal Pb(111) surface is investigated using reflection high-energy electron diffraction. When the temperature is increased from 323 to 590 K. the average terrace width and the average string length at the step edge decrease from 85±25 to 37±16 Å and from 220±33 to 25±8 Å, respectively. Thermal step collapse on the Pb(111) surface near its bulk melting temperature is not observed. Above 530±7 K, the change in the string length at the step edge with temperature becomes small, and the intensity of the (00) beam is significantly decreased. We conclude that partial …