Analysis Of The Effect Of Different Surface Preparation Methods On Corrosion Resistance And Adhesion Strength Of Astm A36 Steel Substrate With Surface Tolerant Epoxy Paint As Coating Material, Irwan Wijaya Santoso, Daffa Aqila, Rini Riastuti, Rizal Tresna Ramadhani
Analysis Of The Effect Of Different Surface Preparation Methods On Corrosion Resistance And Adhesion Strength Of Astm A36 Steel Substrate With Surface Tolerant Epoxy Paint As Coating Material, Irwan Wijaya Santoso, Daffa Aqila, Rini Riastuti, Rizal Tresna Ramadhani
Journal of Materials Exploration and Findings
In the industrial world, to extend the service life of materials, protection methods are carried out to slow down the material's corrosion rate. The protection method that is often used is the coating method. The coating method is a protection method by coating the substrate material using a coating material to prevent contact between the substrate material and the environment. In this research, the substrate material used is ASTM A36 steel and the coating material used is Surface Tolerant Epoxy paint. The independent variable used in this study lies in the surface preparation method which consists of: solvent cleaning, hand …
Effects Of Ti Addition On The Characteristics Of Al-10zn-6mg-2si/Zro2 Composites Produced By Squeeze Casting, Qesha Diva Prameshvara, Pipin Indah Lestari, Bondan Tiara Sofyan
Effects Of Ti Addition On The Characteristics Of Al-10zn-6mg-2si/Zro2 Composites Produced By Squeeze Casting, Qesha Diva Prameshvara, Pipin Indah Lestari, Bondan Tiara Sofyan
Journal of Materials Exploration and Findings
Metal matrix composite (MMC) with 7xxx aluminum matrix is potential for ballistic applications due to the combination of strength, toughness, and light weight. Previous study successfully produced aluminum-based composites with SiC particles which were able to stop type III bullet, however cracks remained on back of the plate. Therefore, in this research, SiC was replaced by zirconia (ZrO2) due to its high fracture toughness. Ti-B grain refiner was added to further improve toughness through grain boundary strengthening mechanism. This research developed 5 vol.% ZrO2 strengthened Al-10Zn-6Mg-2Si composite with addition of Al-5Ti-1B grain refiner produced through squeeze casting …