Stability Analysis Of A Model For The Defect Structure Of Yba2cu3ox, Gregory Kozlowski, Tom Svobodny
Stability Analysis Of A Model For The Defect Structure Of Yba2cu3ox, Gregory Kozlowski, Tom Svobodny
Physics Faculty Publications
Unusual microstructures of YBa2Cu3Ox (123) crystals have been observed. These structures have been shown to pass very high transport currents. A model of the solidification of 123 from a melt with Y2BaCuO5 (211) inclusions indicates that the stability of the 123 interface can depend on the sizes of the 211 inclusions. The observed formations are interpreted in the light of this instability.
Stability Of Growing Front Of Yba(2)Cu(3)O(X) Superconductor In The Presence Of Pt And Ceo(2) Additions, Gregory Kozlowski, Tom Svobodny
Stability Of Growing Front Of Yba(2)Cu(3)O(X) Superconductor In The Presence Of Pt And Ceo(2) Additions, Gregory Kozlowski, Tom Svobodny
Physics Faculty Publications
Distinctive microstructures of textured YBa2Cu3Ox (123) superconductors were examined by scanning electron microscopy and metallurgical microscopy. The samples were synthesized under a residual thermal gradient by using a modified melt textured growth on a Y2BaCuO5 (211) substrate. Also, the unidirectional solidification by a zone‐melting method was performed to fabricate 123 superconducting bars up to 12 cm long placed on the 211 substrate in the horizontal arrangement, with a growth rate R=0.5 mm/h and a temperature gradient of G=20 °C/cm (G/R=400 °C h/cm2). A ramping …