Electrochemical Investigation Into The External Failure Modes Of Oil And Gas Pipelines, Maxwell Goldman

Electronic Thesis and Dissertation Repository

Carbon steel is the material of choice for transmission pipelines for the oil and gas industry across the globe due to its mechanical properties, and low cost. Carbon steel is only resistffxidant, and the types of anions present in the exposure environment. Transmission pipelines are coated with non-conductive polymeric coatings and can be protected by cathodic protection in order to mitigate exterior corrosion. The primary goals of this thesis were to determine the role of anions, cathodic charging with hydrogen, and steel microstructure on different failure modes of carbon steel.

The corrosion mechanism of carbon steel in the presence of …

Galvanic Corrosion Of Copper-Coated Carbon Steel For Used Nuclear Fuel Containers, Thalia E. Standish

Electronic Thesis and Dissertation Repository

Carbon steel vessels coated with ∼3 mm of Cu have been proposed for the permanent disposal of used nuclear fuel in a deep geological repository (DGR) in Canada. In the event of an undetected defect in the Cu coating that exposes the steel substrate, galvanically accelerated corrosion of steel is, in principle, possible. To investigate this scenario, the progression of steel corrosion at the base of novel simulated through-coating defects was monitored electrochemically and imaged non-destructively using X-ray micro-computed tomography (micro-CT) as a function of time, O₂ availability (including anoxic conditions), and coating method (cold spray deposition (with and …

Synchrotron Radiation Analysis Of Daguerreotypes: Surface Characterization, Electrocleaning, And Preservation, Madalena S. Kozachuk

Electronic Thesis and Dissertation Repository

The first commercially viable photographic image, the daguerreotype, captured images from 1839 to 1860. While daguerreotypes provide a significant historical record of 19^th century individuals and events, deterioration now disfigures many of these images. This work describes the application of synchrotron radiation (SR) to the study of daguerreotypes.

Three goals were addressed in this thesis: 1) to utilize SR to further elucidate the physics and chemistry of the daguerreotype and how the surface varies with time, 2) to study the effects of the electrocleaning system on the daguerreotype surface, and 3) to propose suggestions to improve their preservation and …

Evaluating Corrosion Altering Properties Of Thiophene Based Copolymers, Robert Peterson

Dissertations

There is an important and ongoing debate on how or whether conductive polymers (CP) alter corrosion performance with some researchers reporting that CPs ultimately accelerate corrosion and others saying CPs, if understood could possibly replace the world’s best standard for corrosion prevention, i.e., chromium based inhibitors. The primary project goal was to improve our understanding of how CPs alter corrosion chemistry by 1) controlling the polymer structure and 2) in-turn the properties and then 3) targeting the best protocol for fast corrosion kinetic evaluation.

We detail the copolymer synthesis results and shift in corrosion protection properties for …

Corrosion Studies On Lightweight Automotive Alloys: The Effect Of Microstructure And Fundamental Mechanisms, Wilfred J. Binns

Electronic Thesis and Dissertation Repository

Owing to their excellent strength-to-weight ratio and low density, magnesium alloys have the potential to significantly reduce the weight of automobiles leading to decreased emissions and greater range for electrical vehicles. However, the practicality of magnesium alloys for automotive and aerospace applications is severely hindered by their poor corrosion resistance in aqueous environments. Despite intensive research effort, the underlying mechanism(s) responsible for this poor corrosion resistance remains elusive. Further complicating the situation is the presence of secondary microstructures which are necessary for desirable physical properties but lead to microgalvanic coupling which exacerbates the poor corrosion resistance of magnesium alloys. This …

An Experimental And Numerical Investigation Of Flow Accelerated Flibe Corrosion, David B. Weitzel

Nuclear Engineering ETDs

Renewed interest in molten salt reactor technology has brought to light the need for a better understanding of FLiBe corrosion. To this end a flowing FLiBe corrosion test loop was designed to test the flow effects of FLiBe corrosion. The loop consists of a pump, melt tank, and stainless-steel tubing assembly that heats the molten salt to high temperatures and circulates it over test specimens. The experiment has been constructed and has completed initial shakedown testing.

To support the flowing FLiBe experiment, a numerical corrosion model that couples FLiBe electrochemistry, solid metal diffusion, and mass transport was implemented. The model …