Enhancement Of Dielectric Properties With The Addition Of Bromine And Dopamine Modified Barium Titanate Particles To Silicone Rubber, Liang Jiang, David Kennedy, Stephen Jerrams, Tony Betts

Articles

Dual-coated barium titanate (BT) particles were prepared using dopamine (DP) in conjunction with bromine (Br) in order to enhance the dielectric constant of silicone rubber (SR) composites containing evenly distributed BT particles. The results showed that both DP and Br were deposited on the BT particles. The dielectric constant of the SR/BT composite was significantly increased from 3.6 to 4.7 at 1 kHz with the addition of BT modified with dopamine (DP–BT). Moreover, the dielectric constant further rose to 4.9 at 1 kHz when the DP–BT particle was grafted with bromine (Br–DP–BT).

Corrosion Protection Of Aa 2024-T3 Aluminium Alloys Using 3, 4-Diaminobenzoic Acid Chelated Zirconium-Silane Hybrid Sol-Gels, P.C. Rajath Varma, John Colreavy, John Cassidy, Mohamed Oubaha, Colette Mcdonagh, Brendan Duffy

Articles

Organic-inorganic polymers formed by hydrolysis/condensation reactions of alkoxide precursors, such as organically modified silanes (Ormosils) have found applications as electronic, optical and protective coatings. Such coatings possess important characteristics such as chemical stability, physical strength and scratch resistance. Further performance improvement is achieved through the incorporation of zirconium and titanium based nanoparticles, also formed through the sol-gel process. However due to the inherent difference in the reactivity of the precursors, the hydrolysis of each precursor must be carried out separately before being combined for final condensation. Zirconium precursors are commonly chelated using acetic acid or acetyl acetonate prior to hydrolysis, …

Effect Of Organic Chelates On The Performance Of Hybrid Sol–Gel Coated Aa2024-T3 Aluminium Alloys, Rajath Varma, John Colreavy, John Cassidy, Mohamed Oubaha, Colette Mcdonagh, Brendan Duffy

Articles

Sol–gels are organic–inorganic polymers formed by hydrolysis/condensation reactions of alkoxide precursors, primarily silanes, which have found applications as electronic, optical and protective coatings. These coatings possess important characteristics such as chemical stability, physical strength and scratch resistance. Further performance improvement is achieved through the incorporation of zirconium and titanium based nanoparticles, also formed through the sol–gel process. However due to the inherent difference in the reactivity of the precursors, the hydrolysis of each precursor must be carried out separately before being combined for final condensation. Zirconium precursors are commonly chelated using acetic acids, prior to hydrolysis, to lower the hydrolysis …

A Novel Processing Route For The Production Of Nanoparticulate Zinc Oxide Using An Isophthalate Precursor, Grainne Duffy, Declan Mccormack, Suresh Pillai

Articles

Zinc oxide nanoparticles have been processed from a novel isophthalate precursor. In contrast to those processed from an oxalate precursor, this material exhibits three-dimensional, non-directional aggregation behaviour.

Such non-directional aggregation of uniaxial crystallites may allow for the production of structures with a higher proportion of catalytically active surfaces than can be prepared through conventional sol–gel methods. XRD,

FTIR, TEM and SEM were used to characterize the synthesized materials.

Zinc oxide particles synthesized by using isophthalic acid (C6H4-1,3-(COOH)2) are found to be slightly smaller than the previously reported materials prepared through chelation with oxalic acid (H2C2O2・2H2O).