Articles 1 - 3 of 3
Full-Text Articles in Physical Sciences and Mathematics
The Decomposition Of Yba₂Cu₃O₇₋Δ Doped Into Ba₂Yruo₆, H. A. Blackstead, William B. Yelon, M. Kornecki, M. P. Smylie, P. J. Mcginn, Jinbo Yang, Qingsheng Cai, William Joseph James
The Decomposition Of Yba₂Cu₃O₇₋Δ Doped Into Ba₂Yruo₆, H. A. Blackstead, William B. Yelon, M. Kornecki, M. P. Smylie, P. J. Mcginn, Jinbo Yang, Qingsheng Cai, William Joseph James
Physics Faculty Research & Creative Works
One of the persistent criticisms of claims for observation of superconductivity in Ba2YRu1−uCuuO6 (O6) is that the diamagnetism is actually due to the decomposition of the material into YBa2Cu3O7−delta and other phases. We report a series of experiments in which YBa2Cu3O7−delta is doped into Ba2YRuO6 and carried through a series of sintering steps which were followed by magnetization, neutron diffraction, and scanning electron microscopy/microprobe measurements. It was found that the dopant YBa2Cu3O7−delta decomposed and failed to reform with cooling. It is concluded that the O6 phase is the stable high-temperature phase. The Cu released from the Y123 decomposition doped the …
The Effect Of Cu-Doping On The Magnetic And Transport Properties Of La₀.₇Sr₀.₃Mno₃, M. S. Kim, Jinbo Yang, Qingsheng Cai, X.-D. Zhou, William B. Yelon, Paul Ernest Parris, William Joseph James
The Effect Of Cu-Doping On The Magnetic And Transport Properties Of La₀.₇Sr₀.₃Mno₃, M. S. Kim, Jinbo Yang, Qingsheng Cai, X.-D. Zhou, William B. Yelon, Paul Ernest Parris, William Joseph James
Physics Faculty Research & Creative Works
The effects of Cu-doping on the structural, magnetic, and transport properties of La0.7Sr0.3Mn1xCuxO3 (0<=x<=0.20) have been studied using neutron diffraction, magnetization, and magnetoresistance (MR) measurements. All samples show the rhombohedral structure with the R[overline 3]c space-group from 10 K to room temperature (RT). Neutron diffraction data suggest that some of the Cu ions have a Cu3+ state in these compounds. The substitution of Mn by Cu affects the MnO bond length and Mn-O-Mn bond angle resulting from the minimization of the distortion of the MnO6 octahedron. Resistivity measurements show that a metal to insulator transition occurs for the x>=0.15 samples. The x=0.15 sample shows the highest MR([approximate]80%), which might result from the co-existence of Cu3-Cu2+ and the dilution effect of Cu-doping on the double exchange interaction
Neutron Diffraction Studies Of Erni₅₋ₓcoₓ (X=0.68, 1.68, 2.26) Alloys, Z. Zu, William B. Yelon, G. K. Marasinghe, William Joseph James
Neutron Diffraction Studies Of Erni₅₋ₓcoₓ (X=0.68, 1.68, 2.26) Alloys, Z. Zu, William B. Yelon, G. K. Marasinghe, William Joseph James
Physics Faculty Research & Creative Works
ErNi5-xCox alloys were prepared by RF induction melting and analyzed using neutron powder diffraction. Rietveld analysis neutron diffraction data indicates the unit cell volume increases with Co content while the a and c lattice parameters show different dependencies on the composition. the Co atoms show higher affinity for the 3g sites than for the 2c sites. the Co sublattice tends to couple antiferromagnetically to the Er sublattice. the easy magnetization direction is along the c axis.