Full-Text Articles in Nanotechnology
Synthesis Of Lanthanum-Strontium Magnanites By A Hydroxide-Precursor Co-Precipitation Method In Solution And In Reverse Micellar Microemulsion, Vuk Uskoković, Darko Makovec, Miha Drofenik
Synthesis Of Lanthanum-Strontium Magnanites By A Hydroxide-Precursor Co-Precipitation Method In Solution And In Reverse Micellar Microemulsion, Vuk Uskoković, Darko Makovec, Miha Drofenik
Pharmacy Faculty Articles and Research
Nanostructured lanthanum-strontium manganites have been synthesized using two different co-precipitation approaches, one in bulk solution, and the other in reverse micelles of CTAB/1-hexanol/1-butanol/water microemulsion. In both cases, precursor cations were precipitated by alkali precipitating agents. The properties of the material synthesized by using these two methods were compared in order to reveal potential advantages of microemulsion-assisted approach. The influence of the annealing conditions on the properties of synthesized manganites was investigated by using X-ray diffraction, transmission electron microscopy, differential thermal analysis, thermogravimetric analysis and magnetic measurements.
Synthesis Of Nanocrystalline Nickel-Zinc Ferrites Via A Microemulsion Route, Vuk Uskoković, Miha Drofenik
Synthesis Of Nanocrystalline Nickel-Zinc Ferrites Via A Microemulsion Route, Vuk Uskoković, Miha Drofenik
Pharmacy Faculty Articles and Research
Nanostructured NiZn-ferrites were synthesized using a low-temperature co-precipitation method within the reverse micelles of ternary CTAB/1-hexanol/water microemulsions. The influence of pH on the precipitation reaction was investigated. It was found that a higher pH resulted in more crystalline particles. Subsequent oxidation of the ferrous ions precipitate, which leads to the formation of spinel ferrites, is discussed. Diffraction-lines broadening and specific surface area measurements yielded an average particle size of ~ 3 nm. The saturation magnetization of the samples was 20 times smaller than for traditionally synthesized NiZn-ferrites, while the coercivities were 10 - 100 times larger than bulk NiZn-ferrites, which …