Synthesis And Characterization Of Poly(Allyl Methacrylate) Obtained By Free Radical Initiator., Selda Keskin

Allyl methacrylate was polymerized in CCl4 solution by a,a0-azoisobutyronitrile at 50, 60, and 708C. The kinetic curves were autoaccelarated types at 60 and 708C, but almost linear at 508C. Arrhenius activation energy was 77.5 kJ/mol. The polymer was insoluble in common organic solvents. It was characterized by FT-IR, NMR, DSC, TGA and XPS methods. About 98–99% of allyl side groups were remained as pendant even after completion of the polymerization. The spectroscopic and thermal results showed that polymerization is not a cyclopolymerization type, but may have end group cyclization. The high molecular weight is the main cause of a polymer …

The Evaluation Of Some Flexural Properties Of Denture Base Resin Reinforced With Various Aesthetic Fibers, Selda Keskin

No abstract provided.

Stoichiometric Network Analysis And Associated Dimensionless Kinetic Equations. Application To A Model Of The Bray-Liebhafsky Reaction, Zeljko D. Cupic

Zeljko D Cupic

No abstract provided.