Environment-Induced Degradations In A Target Structural Material For Transmutation Applications, Ramprashad Prabhakaran
Environment-Induced Degradations In A Target Structural Material For Transmutation Applications, Ramprashad Prabhakaran
UNLV Theses, Dissertations, Professional Papers, and Capstones
This investigation is focused on the evaluation of stress corrosion cracking (SCC) and localized corrosion behavior of Type 422 stainless steel in aqueous environments at ambient and elevated temperature. The results of constant load SCC testing using smooth specimens showed no failure in the neutral solution but a threshold stress of 97 ksi was observed in the 90°C acidic environment. SCC testing by the slow-strain-rate test method indicate that the time-to-failure, true failure stress and ductility parameters were gradually reduced with increasing temperature, showing more pronounced effect in the acidic solution. The application of a controlled cathodic potential showed further …
Study Of Geometric Effects On Local Corrosion Rates For Lbe Loop, Chao Wu
Study Of Geometric Effects On Local Corrosion Rates For Lbe Loop, Chao Wu
UNLV Theses, Dissertations, Professional Papers, and Capstones
Corrosion is an extremely important issue in nuclear cooling system applications. Many scientific and engineering efforts have been contributed to the research of finding an ideal material, which has resistance to corrosive Lead Bismuth Eutectic (LBE). A Delta Loop was designed and constructed in Los Alamos National Lab (LANL) to obtain the experimental data. This loop is a multi-section closed system that differs in diameter from one part to another. As a result, an intensive study on the geometry effect is hence necessary and valuable. In this thesis, this problem was simulated by commercial software STAR-CD. Results provide a good …
Investigation Of The Corrosion Of Steel By Lead-Bismuth Eutectic (Lbe) Using Scanning Electron Microscopy And X-Ray Photoelectron Spectroscopy, Daniel Koury
UNLV Theses, Dissertations, Professional Papers, and Capstones
Lead Bismuth Eutectic (LBE) has been proposed for use in programs for accelerator transmutation of waste. LBE is the leading candidate material as a spallation target and an option for the sub-critical blanket coolant. The corrosion of 316 and 316L stainless steels by LBE has been studied using UNLV's facilities for Scanning Electron Microscopy (SEM) and X-ray Photoelectron Spectroscopy (XPS). We have compared exposed and unexposed samples and studied the differences. Some amount of surface contamination is present on the samples and has been removed by ionbeam etching. The unexposed samples reveal typical stainless steel characteristics: a chromium oxide passivation …