Nuclear Engineering Commons^™

Physical Properties Of Copper Niobium Nanolamellar Composites Fabricated By Accumulative Roll Bonding, Jared Justice

Nuclear Engineering ETDs

Nanolamellar composites with high interface density have increased strength due to interfaces serving as barriers to dislocation movement and high radiation damage resistance. However, these interfaces also serve as barriers to electron motion, reducing the electrical resistivity and thermal conductivity. This work seeks to understand the inherent tradeoff between strength and physical properties of nanolamellar composites produced by accumulative roll bonding with layer thickness ranging from 25 nm to 193 nm. The electrical resistivity was investigated over temperatures ranging from 2 K to 300 K. The effect of longitudinal rolling and cross rolling was also investigated. Electrical resistivity results were …

An Experimental And Numerical Investigation Of Flow Accelerated Flibe Corrosion, David B. Weitzel

Nuclear Engineering ETDs

Renewed interest in molten salt reactor technology has brought to light the need for a better understanding of FLiBe corrosion. To this end a flowing FLiBe corrosion test loop was designed to test the flow effects of FLiBe corrosion. The loop consists of a pump, melt tank, and stainless-steel tubing assembly that heats the molten salt to high temperatures and circulates it over test specimens. The experiment has been constructed and has completed initial shakedown testing.

To support the flowing FLiBe experiment, a numerical corrosion model that couples FLiBe electrochemistry, solid metal diffusion, and mass transport was implemented. The model …