Use Of Positron Annihilation Spectroscopy For Stress-Strain Measurements: Quarterly Progress Report (June 01 – August 31, 2004), Ajit K. Roy

Transmutation Sciences Materials (TRP)

Highlights of Test Results:

• Residual stress measurements by the RC method on cold-worked specimens showed tensile residual stresses in austenitic stainless steel. However, compressive residual stresses were observed in martensitic stainless steel. This difference may be attributed to the difference in metallurgical phases and microstructures resulting from different thermal treatments imparted to them.

• Residual stress measurements by both ND and RC techniques on welded specimens showed similar patterns. Welded specimens consisting of similar material showed tensile residual stresses in the vicinity of the fusion line (FL). However, welded specimens consisting of dissimilar materials (austenitic and martensitic stainless steel …

Use Of Positron Annihilation Spectroscopy For Stress-Strain Measurements, Ajit K. Roy

Transmutation Sciences Materials (TRP)

The purpose of this collaborative research project involving the University of Nevada Las Vegas (UNLV) and Idaho State University (ISU) is to evaluate the feasibility of determining residual stresses of welded, bent (three-point-bend), and cold-worked engineering materials using a new nondestructive technique based on positron annihilation spectroscopy (PAS). The proposed technique is to use γ-rays from a small MeV electron linear accelerator (Linac) to generate positrons inside the test sample via 2 pair production. This method can be used for materials characterization and investigation of defects in thick samples that usually cannot be accomplished by conventional positron technique or other …

Use Of Positron Annihilation Spectroscopy For Stress-Strain Measurements, Ajit K. Roy

Transmutation Sciences Materials (TRP)

Metals and alloys, when subjected to tensile loading beyond a limiting value, can undergo plastic deformation resulting in lattice defects such as voids and dislocations. These imperfections may interact with the crystal lattice, producing a higher state of internal stresses characterized by reduced ductility. Residual stresses can also be generated in welded structures due to rapid rate of solidification, and dissimilar metallurgical microstructures between the weld and the base metals. Premature failures can be experienced in engineering metals and alloys due to the presence of these residual stresses. Specific thermal treatments commonly known as stress relief operations can relieve these …