Phase Transitions In Mechanically Milled Mn-Al-C Permanent Magnets, Michael J. Lucis, Timothy E. Prost, Xiujuan Jiang, Meiyu Wang, Jeffrey E. Shield

Department of Mechanical and Materials Engineering: Faculty Publications

Mn-Al powders were prepared by rapid solidification followed by high-energy mechanical milling. The rapid solidification resulted in single-phase ε. The milling was performed in both the ε phase and the τ phase, with the τ-phase formation accomplished through a heat treatment at 500 °C for 10 min. For the ε-milled samples, the conversion of the ε to the τ phase was accomplished after milling via the same heat treatment. Mechanical milling induced a significant increase in coercivity in both cases, reaching 4.5 kOe and 4.1 kOe, respectively, followed by a decrease upon further milling. The increase in coercivity was the …